Construction of tissue engineered cartilage by using AdLacZ gene modified goat auricular chondrocytes and Pluronic F127 scaffold

Q Chang,XL Zhang,XQ Jiang

DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.32.002

2007-01-01

Abstract:Aim: To observe the chondrogenesis after AdLacZ gene modified goat auricular chondrocytes were combined with Pluronic F127 scaffold and injected into nude mice subcutaneously, so as to provide preliminary parameters for future chondrogenic differentiation factor gene therapy in cartilage reconstruction. Methods: The experiment was carried out in Shanghai Ninth People's Hospital affiliated to Shanghai Jiao Tong University Medical School from November 2004 to December 2006. 1Health male goat of 26-30 kg and twenty-four 6 weeks old BALB/c nude mice of 20 g were selected. Goat auricular chondrocytes were cultured in vitro and transfected with AdLacZ over-expression viruses, and gene transfer efficiency was tested. 2Those gene-modified chondrocytes were then combined with biodegradable Pluronic F127 scaffold and injected at 2 points in 6 nude mice subcutaneously. Samples were collected 2 and 4 weeks postoperatively with 6 cases at each time point. Another 18 nude mice were selected and subjected to the previous process, and the non-transfected chondrocytes with scaffold, cells along or scaffold along were regarded as control group with 6 animals in each group. 3All samples were given H-E staining, and alcian blue staining, and the 4-week samples were given X-gal staining, and collagen II immunohistochemistry staining. Results: Twenty-four nude mice were involved in the result analysis. An MOI of 50 pfu/cell produced optimal effects in transfer efficiency over 80%. At week 2, immature cartilage-like tissue formed at AdLacZ treated chondrocytes injection sites, and H-E staining showed that the outside was fiberlike encapsulation, while the middle part was composed of immature chondrocytes. At week 4, a little of comparatively mature cartilage was observed in the middle of the sample; alcian blue staining appealed there was deep blue nidulant cartilage, and type II collagen positive staining was detected in a few cells. X-gal staining suggested that the cells were derived from the implanted cartilage and scaffold composite. Non-transfected chondrocytes plus F127 group showed similar HE and type II collagen expression as the AdLacZ transfected experimental group, but X-gal staining was negative. While no cartilage formation was found in cells along or F127 alone samples within 4 weeks. Conclusion: Adenovirus gene transfection achieved comparatively high transfer efficiency on primary cultured chondrocytes. Pluronic F127 scaffold is a suitable scaffold material for tissue engineered cartilage regeneration.