Abstract:An experimental study is performed on the microstructure transformation induced by rapid laser welding in the different regions of Zr61.4Cu27.8Al4Ni6Y0.8 bulk metallic glass (BMG). The laser input energy has a remarkable influence on the microstructure and microhardness of the Zr-based BMGs. The microstructures in different regions of as-welded joints are diverse. Crystallization happens in heat-affected zone (HAZ) with crystalline dendritic phase of CuZr, which results in the deterioration of the microhardness to 434.9 ± 17.1 HV in HAZ, much lower than that of parent material as 517 ± 5.0 HV. Meanwhile, the element profiles indicate that intragranular segregation of Cu element occurs during the crystallization process. In the center of molten zone (MZ), the structure is fully amorphous and its hardness is close to that of parent material. In the region transiting from MZ to HAZ, some nano-grains with an average size of 20–50 nm are identified. In addition, several flower-like nanostructured grains of Y2O3 phase with a size ranging from 50 to 80 nm are formed in MZ’s matrix. The nanocrystallization is believed to be responsible for the enhancement of the Vickers hardness up to 560.1 ± 8.4 HV in this region.Graphic AbstractRapid laser processing induces three kinds of microstructures in Zr61.4Cu27.8Al4Ni6Y0.8 bulk metallic glasses, i.e., the severe crystallization of CuZr phase in heat affected zones (HAZ), the nano-grains in the region transiting from molten zone (MZ) to HAZ, and the fully amorphous structure in the center of MZ, which consequently results in the diverse microhardness in spatial distribution.

Micro-Electro-Discharge Machining of Bulk Metallic Glasses

Anodic Dissolution Behavior of a Zr-based Bulk Metallic Glass and the Electrochemical Machining of Small Structures with High Geometrical Precision and Good Surface Quality

Finite element simulation and experimental investigation of forming micro-gear with Zr–Cu–Ni–Al bulk metallic glass

Enhanced mechanical properties of Zr65Cu15Ni10Al10 bulk metallic glass by simultaneously introducing surface grooves and multiple shear bands

Micro Array Hole Formation in Glass Using Electrochemical Discharge Machining

Controlling the Mechanical Properties of Bulk Metallic Glasses by Superficial Dealloyed Layer

Microstructural heterogeneities governing the deformation of Cu47.5Zr47.5Al5 bulk metallic glass composites

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Ductile Bulk Metallic Glass by Controlling Structural Heterogeneities

Additive Manufactured Large Zr-Based Bulk Metallic Glass Composites with Desired Deformation Ability and Corrosion Resistance

Effects of processing parameters on the surface roughness of Zr-based bulk metallic glass processed by wire electrical discharge machining

Pronounced Ductility in CuZrAl Ternary Bulk Metallic Glass Composites with Optimized Microstructure Through Melt Adjustment

Microstructure and Mechanical Properties of Porous Zr55Cu30Al10Ni5 Bulk Metallic Glass Fabricated by Spark Plasma Sintering Process

Microstructure Transformation in Different Regions of Zr61.4Cu27.8Al4Ni6Y0.8 Bulk Metallic Glass Induced by Rapid Laser Welding

Micro-back-extrusion of a bulk metallic glass

Microstructure evolution and mechanical properties of Cu46Zr47Al7 bulk metallic glass composite containing CuZr crystallizing phases

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Microstructural Tailoring and Improvement of Mechanical Properties in CuZr-based Bulk Metallic Glass Composites

Influence of the microstructure on mechanical properties of SLM additive manufacturing Fe-based bulk metallic glasses

Effect of In-Situ Crystalline Phases on the Mechanical Properties and Energy Release Behaviors of Zr55Ni5Al10Cu30 Bulk Metallic Glasses

Microstructure and compressive/tensile characteristic of large size Zr-based bulk metallic glass prepared by laser solid forming