CHARACTERIZATION OF IMMOBILIZED TANNIN ON MACROPOROUS SPHERICAL CELLULOSE AND ITS APPLICATION IN FINING CHINESE RICE WINE

Ling CHEN,Zhengfu KOU,Zuozhen LIU,Banghe JIANG,Xingyan WU

DOI: https://doi.org/10.3321/j.issn:1001-5493.2006.05.009

2006-01-01

Abstract:Immobilized tannin, a novel polymer, was synthesized by coupling tannin with macro porous spherical cellulose. By Mercury porosimetry, it had the following characteristics: average pore diameter 70 nm, specific surface area 161.39 m2/g, pore volume 13.53 ml/g. Row rate-pressure curve showed that it had good mechanical property and could work up to the pressure of 0.7 Mpa. The nice chemical stability and insolubility of the immobilized tannin were proved by soaking in 65% ethanol and 4% acetic acid, respectively. When 800ml Chinese rice flowed through the column packed with 4ml immobilized tannin, the effluent appeared clear, transparent and maintained its original flavor. The 65.7% high-molecular protein (Mw ≥ 10 kD) in the original Chinese rice wine was removed, in the meantime total protein content was reduced by 33.4%, while the content of amino nitrogen kept unchanged; and the content of iron ion reduced from 7.79 × 10-8 mol/L to 5.89 × 10-9 mol/L, other components remaining intact. The treated wine possessed excellent stability in the hop-up test and cryopreservation test. The immobilized tannin could be regenerated by 0.1 mol/L HC1 and reused many times.