Chemical Route to Yb 14 MgSb 11 Composites with Nanosized Iron Inclusions for the Reduction of Thermal Conductivity
Christopher J. Perez,Zhijie Chen,Willie B. Beeson,Sevan Chanakian,Kai Liu,Sabah K. Bux,Susan M. Kauzlarich
DOI: https://doi.org/10.1021/acsaem.1c00163
IF: 6.4
2021-03-18
ACS Applied Energy Materials
Abstract:The rapid rise of atmospheric CO<sub>2</sub> has spurred keen research interest in sustainable energy technologies including thermoelectric materials which can reliably and robustly turn heat directly to electricity. Yb<sub>14</sub>MnSb<sub>11</sub> has been the material of intense study because of its high thermoelectric figure of merit, <i>zT</i>. A structural analogue, Yb<sub>14</sub>MgSb<sub>11</sub>, is also of interest as it has a higher average <i>zT</i> () and a comparable peak <i>zT</i> (1.3 vs 1.2) to Yb<sub>14</sub>MnSb<sub>11</sub>. We have shown that Yb<sub>14</sub>MgSb<sub>11</sub> can be composited with micron-sized iron particles with significant improvements to the thermoelectric power factor (PF) and mechanical properties. In this work, we successfully employ a rapid high-temperature <i>in situ</i> reaction to create well-dispersed nanoscale (<100 nm) iron inclusions in the bulk Yb<sub>14</sub>MgSb<sub>11</sub> matrix <i>via</i> the decomposition of FeSb<sub>2</sub> into Fe and Sb. The incorporation of nanoscale iron into Yb<sub>14</sub>MgSb<sub>11</sub> further reduces the lattice thermal conductivity (κ<sub>l</sub>), when compared to the previously published micron iron composites, due to an increase in phonon scattering. As a result of the synchronous decrease in thermal conductivity and resistivity, the 7.3 vol % Fe sample retains the <i>zT</i> of Yb<sub>14</sub>MgSb<sub>11</sub> while achieving a 43% PF improvement.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00163?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00163</a>.PXRD of FeSb<sub>2</sub> compared with the calculated diffraction pattern; plots of Rietveld refinements of all phases investigated in this study; heating and cooling resistivity, Seebeck, and diffusivity data; comparison of SEM <i>Z</i>-contrast for Yb<sub>14</sub>MgSb<sub>11</sub> + 6 Vol % iron composites prepared from FeSb<sub>2</sub> versus micron-sized Fe; SEM BSE image of the Yb<sub>14</sub>MgSb<sub>11</sub> + 6 Vol % iron composite from FeSb<sub>2</sub> after annealing at 1273 K for 168 h; topological and <i>Z</i>-contrasted SEM images at 500×, 1000×, 2500×, and 50,000× for all composite samples studied; and FORC distributions for samples prepared from FeSb<sub>2</sub> and micron-sized iron (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00163/suppl_file/ae1c00163_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels