High Temperature (Nabi)0.48◻0.04bi2nb2o9-Based Piezoelectric Ceramics

Zhi-Gang Gai,Jin-Feng Wang,Ming-Lei Zhao,Chun-Ming Wang,Guo-Zhong Zang,Bao-Quan Ming,Peng Qi,Shujun Zhang,Thomas R. Shrout

DOI: https://doi.org/10.1063/1.2216355

IF: 4

2006-01-01

Applied Physics Letters

Abstract:The effect of (LiCe) substitution for A site on the properties of (NaBi)0.48◻0.04Bi2Nb2O9 (NB◻N)-based ceramics was investigated. The coercive fields (EC) of NB◻N)-based ceramics were significantly decreased from 61.0to32.5kV∕cm and the Curie temperature (TC) gradually decreases from 820to803°C with increasing the (LiCe) modification. The piezoelectric coefficient d33, planar coupling factor kp, and mechanical quality factor Q of (NaBi)0.38(LiCe)0.05◻0.14Bi2Nb2O9 ceramic were found to be 27pC∕N, 11.2%, and 2600, respectively, together with the high TC (∼809°C) and stable piezoelectric properties, demonstrating that the (LiCe) modified NB◻N-based material a promising candidate for high temperature applications.