A new method for evaluating the thrombus formation on biomaterials in vitro
Li-feng Yang,Ting-fei Xi,Jian-xia Xu,Ting-ting Guo,Zi-yi Wan,Zhao-xu Wang
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.45.032
2008-01-01
Abstract:BACKGROUND: Cardiovascular stents and some materials contacted with blood have been developing rapidly. However, there is not a uniform method to evaluate the thrombosis of biomaterials at present. OBJECTIVE: To observe the relationship between the concentration of fibrinogen and thrombosis, and establish a new method for evaluating the thrombus formation on biomaterials in vitro. DESIGN, TIME AND SETTING: A control observational experiment of material science was performed in the Testing Center for Medical Device of National Institute for the Control of Pharmaceutical and Biological Product from December 2007 to July 2008. MATERIALS: One healthy Japanese rabbit, clean grade and weighing 2.5 kg, was used in the experiment. Glass was the product of Yancheng Rongkang Glassware CO., LTD.. Medical silicone rubber and polyethylene were the products of Tianjin plastic research institute. METHODS: Blood samples were drawn from the heart of rabbit with 3.8% sodium citrate for partial anticoagulation. Then, a part of sodium citrate was added into the partial anticoagulation blood for complete anticoagulation every 3 minutes. The concentration of fibrinogen was measured in plasma after separation. The blood samples of partial anticoagulation obtained with the same method as above were divided into four groups: positive, silicone rubber, polyethylene and negative groups. In the positive, silicone rubber, polyethylene groups, the blood samples of partial anticoagulation were contracted with glass, silicone rubber and polyethylene, respectively. The blood samples in the negative group were not contracted with anything. Fifteen minutes later, the sodium citrate was added in the four groups for complete anticoagulation. The concentration of fibrinogen was measured in plasma after separation. MAIN OUTCOME MEASURES: The relationship between concentration of fibrinogen and thrombosis were observed. And the extents of thrombus formation in the positive, silicone rubber, polyethylene groups were compared. RESULTS: With the increase of exposure time of the partial anticoagulation blood in vitro, the amount of thrombus formation increased gradually. The later the anticoagulant was added, the lower the concentration of fibrinogen was. The results suggested that the concentration of fibrinogen was inversely proportional to the amount of thrombosis. The concentrations of fibrinogen in the negative, silicone rubber, polyethylene groups were significantly higher than that in the positive group (t =2.842-3.737, P < 0.05). There was no significant difference in concentrations of fibrinogen between the silicone rubber and polyethylene groups (t=0.747, P > 0.05), but the concentrations of fibrinogen in both of them were significantly lower than that in the negative group (t =3.691, 3.192, P < 0.05). CONCLUSION: The measurement of fibrinogen concentrations can be used as a screen test for evaluation of thrombus formation on biomaterials, which is proved by glass, polyethylene and silicone rubber. The findings show that the blood compatibility of silicone rubber and polyethylene is better than glass.