Irreversible Transition from GaO 6 Octahedra to GaO 4 Tetrahedra for Improved Electrochemical Stability in Ga-Doped Li(Ni 0.9 Co 0.1 )O 2
Xinru Ge,Jing Yu,Liheng Zhu,Zeneng Deng,Jiliang Zhang,Chi-Liang Chen,Wei-Hsiang Huang,Bo Hao Chen,Chung-Kai Chang,Hongyu Chen,Ruirui Zhao
DOI: https://doi.org/10.1021/acs.inorgchem.0c03211
IF: 4.6
2021-02-12
Inorganic Chemistry
Abstract:Trace doping is an efficient way to improve the stability of nickel-rich layered cathodes for lithium-ion batteries, but the structural origin of such improvement, rather than a simple replacement, has been rarely explored. Herein, Ga dopants have been introduced into a nickel-rich host, LiNi<sub>0.9</sub>Co<sub>0.1</sub>O<sub>2</sub>, by a combination of coprecipitation and the solid-state sintering method. Structural analyses based on high-resolution synchrotron powder diffraction data and X-ray absorption spectra suggest that Ga preferentially sits in the NiO<sub>6</sub> slabs, resulting in reduced Ni/Li cationic mixing and depressed lattice vibration. Due to the smaller dissociation energy of Ga–O bonds, some Ga<sup>3+</sup> cations migrate first toward Li layers upon delithiation and form the GaO<sub>4</sub> tetrahedral symmetry irreversibly during the electrochemical process, which acts as a pillar in the subsequent electrochemical processes. As a result, the doped material exhibits both improved cycling performance and rate capability under a high operating voltage (4.5 V) due to the stabilized structure in the lithiation/delithiation process. This study illustrates how a dopant enhances the electrochemical stability in views of both pristine and charged structure and suggests that a positive effect is expected from the dopant favoring the tetrahedral symmetry (<i>e.g.</i>, Al).The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.inorgchem.0c03211?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.inorgchem.0c03211</a>.Ga 3d XPS spectra of Ga-LNCO; morphologies and synchrotron XRD data of LNCO; Rietveld refinements on LNCO; Rietveld refinements on Ga-LNCO with different occupation sites; Li diffusion coefficients calculated from GITT; EIS spectra of pristine electrodes; SEM images of the materials after cycling; Pawley refinements on the <i>ex situ</i> XRD data of electrodes after 100 cycles; refined structural parameters; electrochemical performance of LiNi<sub>0.9</sub>Co<sub>0.1</sub>Co<sub>2</sub> reported in the literature; and fitted electrical parameters from EIS (<a class="ext-link" href="/doi/suppl/10.1021/acs.inorgchem.0c03211/suppl_file/ic0c03211_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, inorganic & nuclear