Microstructure and mechanical properties of in situ TiC and Nd2O3 particles reinforced Ti–4.5wt.%Si alloy composites
Xinjiang Zhang,Yibin Li,Guangping Song,Yue Sun,Qingyu Peng,Yuxin Li,Xiaodong He
DOI: https://doi.org/10.1016/j.matdes.2011.04.003
IF: 9.417
2011-01-01
Materials & Design
Abstract:Highlights ► (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites were in situ synthesized. ► The phase components and microstructures of the composites were investigated. ► In situ reinforcements improve the mechanical properties of the matrix alloy. Abstract (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites were in situ synthesized by a non-consumable arc-melting technology. The phases in the composites were identified by X-ray diffraction. Microstructures of the composites were observed by optical microscope and scanning electron microscope. The composite contains four phases: TiC, Nd 2 O 3 , Ti 5 Si 3 and Ti. The TiC and Nd 2 O 3 particles with dendritic and near-equiaxed shapes are well distributed in Ti–4.5 wt.%Si alloy matrix, and the fine Nd 2 O 3 particles exist in the network Ti + Ti 5 Si 3 eutectic cells and Ti matrix of the composites. The hardness and compressive strength of the composites are markedly higher than that of Ti–4.5 wt.%Si alloy. When the TiC content is fixed as 10 wt.% in the composites, the hardness is enhanced as the Nd 2 O 3 content increases from 8 wt.% to 13 wt.%, but the compressive strength peaks at the Nd 2 O 3 content of 8 wt.%. Keywords A. Metal matrix composites F. Microstructure G. X-ray analysis 1 Introduction Titanium and its alloys have been widely used as the ideal matrix for developing reinforced metal matrix composites because of their high specific modulus, high specific strength, high fracture toughness and heat resistance [1–3] . To the Ti–Si alloys, the intermetallic compound Ti 5 Si 3 phase, as the reinforcement in the titanium matrix, can significantly improve some properties of the titanium matrix because of its high melting point (2130 °C), low density (4.32 g/cm 3 ), good oxidation resistance and creep resistance [3–7] . Particle reinforced titanium matrix composites (PRTMCs) have considerable potential for structural applications in fields of aerospace and automobile industries for the improvement of various mechanical properties (especially stiffness, strength and wear resistance), over conventional titanium alloys [8,9] . In recent years, in situ compositing technology has been developed to prepare PRTMCs, such as self-propagation high-temperature synthesis [10] , rapid solidification [11,12] and casting [1,13] . This technology offers an attractive set of advantages: low fabrication cost, stable interface, fine reinforcement. The numerous works have shown that many particle-reinforcements can been directly fabricated in the titanium matrix composites by the in situ technology. Especially, TiC particle is a preferential candidate as the reinforcement due to its high hardness, high modulus and high flexural strength [14–16] . Moreover, the rare earth oxide (RE 2 O 3 ) was proved to be valuable to grain refinement, fatigue resistance and thermal stability [17,18] . Thus, for developing new structural materials to extend the application of in situ PRTMCs, it is promising for the introduction of in situ TiC and RE 2 O 3 particles in the titanium alloys to obtain excellent mechanical property. In the present work, (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites were in situ synthesized by the direct melting reaction between Ti, Si, Nd, C and SiO 2 . The phase components and microstructures of the composites were systematically investigated, and the synergistic effect of TiC and Nd 2 O 3 reinforcements on the mechanical properties of the composites was also studied. 2 Experimental procedure (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites utilizing the reaction between Ti, Si, Nd, C and SiO 2 were in situ synthesized through melting in a non-consumable vacuum arc remelting furnace. The raw materials were sponge Ti (>99.9% purity), Si (>99.9% purity), Nd (>99.9% purity), C powder (>99.9% purity) and SiO 2 powder (>99.9% purity). To investigate the morphologies and enhanced effect of Nd 2 O 3 reinforcement, three different contents of neodymium dioxide were designed in the composites. Moreover, Ti–4.5 wt.%Si alloy was also prepared. In order to ensure the chemical homogeneity of the composites, each ingot was turned over and remelted for five times. The weight percentage of reactants and theoretical weight percentage of TiC and Nd 2 O 3 products are listed in Table 1 . Phase identification of the samples was carried out via X-ray diffraction (XRD) using Rigaku D/max-2200 diffractometer with Cu Kα radiation. The metallographical samples were prepared using conventional grinding and mechanical polishing techniques. Microstructural analysis was performed using the DMM-660C optical microscopy and the HITACHI S-3700N scanning electron microscopy (SEM) with energy dispersive (EDS) analysis. Vicker’s hardness was evaluated via the HVS-1000 digital Vickers sclerometer with the load of 4.9 N and a load-dwell time of 20 s. The hardness value was the average result of eight indentations for each sample. The compressive properties of the composites ware conducted at room temperature on the Instron 8801 testing machine with the initial strain rate is 1 mm/min. The compressive specimens had a gauge of 5 mm × 5 mm square section and 10 mm length. In compressive test, the loading was along the length direction of specimens. Three compressive specimens were tested for each material and the reported results are average values. 3 Results and discussion 3.1 Phase analysis Fig. 1 shows XRD patterns of 1#–4# samples. From XRD pattern of 1# sample, it is found that Ti–4.5 wt.%Si alloy only contains Ti and Ti 5 Si 3 phases. However, the other samples (2#–4#) include four phases, namely Nd 2 O 3 , TiC, Ti and Ti 5 Si 3 . The results of XRD analysis confirm that (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites can be in situ fabricated via the direct melting reaction among the raw materials Ti, Si, Nd, C and SiO 2 . In this work, the multiple phases Ti 5 Si 3 , TiC and Nd 2 O 3 are synthesized according to following two reactions: (1) 6 Ti + 4 Nd + 3 SiO 2 + C = Ti 5 Si 3 + 2 Nd 2 O 3 + TiC (2) ( 5 + x ) Ti + 3 Si = Ti 5 Si 3 + x Ti In order to verify the thermodynamic feasibility of in situ reaction involved in this work, the Gibbs free energy (Δ G ) and the reaction formation enthalpy (Δ H ) for reactions (1) and (2) have been calculated using the thermodynamic data from Ref. [19] . The calculation results are shown in Fig. 2 . From Fig. 2 , the negative Gibbs free energy (Δ G ) and the negative reaction formation enthalpy (Δ H ) for the reactions (1) and (2) indicate that the formation of Ti 5 Si 3 , TiC and Nd 2 O 3 multiple phases are favorable and exothermic from the viewpoint of thermodynamics. Thus it is feasible to synthesize the (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites through reactions (1) and (2) during melting. 3.2 Microstructure evolution Fig. 3 shows the optical micrographs of 1#–4# samples. For 1# sample (Ti–4.5 wt.%Si alloy), the continuous and quasi-continuous network-shape Ti + Ti 5 Si 3 eutectic cells distribute in the matrix Ti ( Fig. 3 a). In comparison with 1# sample, in 2#–4# samples, the reinforcements are uniformly distributed in the Ti–4.5 wt.%Si alloy matrix, as observed in Fig. 3 b–d. The morphologies of reinforcements exhibit dendritic and near-equiaxed shapes in the optical micrographs of the composites. The results of EDS indicate that the dendritic or near-equiaxed shaped and light-colored reinforcements are TiC, and the near-equiaxed shaped but dark-colored reinforcements are Nd 2 O 3 particles. Moreover, the grain size of TiC and Nd 2 O 3 particles becomes obviously bigger with the increase of the Nd content in the composites. In order to further examine the morphologies and distribution of Ti 5 Si 3 , TiC and Nd 2 O 3 , the backscattered SEM micrographs of 2# and 4# samples were conducted, as shown in Fig. 4 . The Nd 2 O 3 reinforcements show near-equiaxed and dendritic grains, as shown in Fig. 4 a and c. Moreover, in the magnified photographs of white boundary marked region in Fig. 4 a and c, it can be clearly shown that the continuous and quasi-continuous network-shape Ti + Ti 5 Si 3 eutectic cells also distribute in the composites ( Fig. 4 b and d). The introduction of in situ reinforcements does not change the morphology of Ti + Ti 5 Si 3 eutectic cells in Ti–4.5 wt.%Si alloy. However, a lot of fine Nd 2 O 3 particles exist in the Ti + Ti 5 Si 3 eutectic cells and Ti matrix of the composites, as shown in Fig. 5 . The different shapes of TiC and Nd 2 O 3 particles are related to their crystal structures and solidification paths. To the particle reinforced titanium matrix composites fabricated by the casting technique, several workers have studied the microstructural characterization of in situ particle (TiC or Y 2 O 3 ), indicating that the formation of in situ reinforcement would undergo nucleation and growth during solidification [16,20] . Moreover, it should be pointed out that TiC exhibits a NaCl-type structure [21] and Nd 2 O 3 has a Mn 2 O 3 -type crystal structure [17] . These two crystal structures show high geometric symmetry. Thus, when the primary TiC and Nd 2 O 3 nucleate, the growth rate in symmetric crystal planes is similar, leading to the formation of equiaxed spherical particles. As the temperature decreased, the abundant heterogeneous particles in the liquid easily formed at the solid–liquid interface during the solidification process. Some positions at the solid–liquid interface became unstable to grow into dendritic grains. Moreover, the abundant fine Nd 2 O 3 particles are secondary precipitates in the Ti + Ti 5 Si 3 eutectic cells and Ti matrix of the composites ( Fig. 5 ). According to Ti–Nd phase diagram [22] , the maximum solid solution ability of Nd in βTi is about 7 wt.% while it does not nearly solid–solute in αTi at room temperature. Thus, Nd atoms dissolved in βTi reacted with oxygen to form fine Nd 2 O 3 particles in the solidification process. 3.3 Mechanical properties The Vicker’s hardness (HV) and the compressive properties (ultimate compressive strength (UCS), fracture strain ( ε )) of 1#–4# samples are shown in Table 2 . Fig. 6 shows SEM micrographs of the typical hardness indentations in Ti–4.5 wt.%Si alloy ( Fig. 6 a) and the composites ( Fig. 6 b). From Table 2 and Fig. 6 , it is obvious that the hardness of the composites (2#–4# samples) is higher than that of unreinforced Ti–4.5 wt.%Si alloy (1# sample). According to Table 2 , the hardness of the composites increases gradually with the increase of weight fraction of Nd 2 O 3 . The reinforcements play a significant role in the contribution of the hardness enhancement of the composites. For example, Chen et al. [23] have confirmed that the addition of dispersed TiC and La 2 O 3 particles to tungsten matrix by powder metallurgy is beneficial to the hardness of tungsten. Huang et al. [24] have also reported that in situ TiB reinforcements fabricated by reaction hot pressing can increase the hardness of Ti–6Al–4V matrix. The higher hardness of the composites is due to the reinforcements. In this work, it is well known that the ceramic TiC and Nd 2 O 3 particles have higher hardness than the Ti matrix, which is helpful to improve the hardness of the composites. To the compressive properties, compared with the matrix Ti–4.5 wt.%Si alloy (1# sample), the ultimate compressive strength of the composites (2#–4# samples) are significantly improved due to the in situ formation of Nd 2 O 3 and TiC particles, whereas the fracture strain of the composites shows reverse effect. Moreover, when the TiC content is fixed as 10 wt.%, the compressive strength of the composites peaks at 8 wt.% of Nd 2 O 3 particles. The typical SEM micrographs of the fractured surfaces for the matrix Ti–4.5 wt.%Si alloy and the composites are shown in Fig. 7 . There was a large difference in the appearance of fracture surfaces between the matrix alloy and the composite in the same magnification. The smooth and flat surface and the tiny cleavage facet are found on the fractured surface of the matrix alloy ( Fig. 7 a). The fractured surface of the composite is coarse, and some pulled out and cracked particles are observed, indicating that they could undertake load during compression test, as shown in Fig. 7 b–d. The introduction of in situ TiC and Nd 2 O 3 particles can significantly improve the compressive strength of Ti–4.5 wt.%Si alloy. From previous reports in Refs. [25,26] , the strengthening reasons of the in situ particles reinforced composites may be mainly that the hard particles act as the obstacles to hinder the motion of dislocations. To (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites, when the composites bears the load and the plastic deformation of the material is caused, the load transfers from the soft matrix to the hard Nd 2 O 3 and TiC reinforcements, the dislocations need to overcome the higher resistance, so the strength and modulus of the composite reinforced with Nd 2 O 3 and TiC particles are improved. Furthermore, the interaction of different dislocation areas also contributes to the improvement of the strength of the composites. The strengthened mechanical properties of the composites may be due to the grain refinement caused by the presence of TiC and Nd 2 O 3 particles . According to the Hall–Petch equation [26,27] , (3) σ = σ 0 + kd - 1 / 2 where σ 0 is either a frictional stress resisting to the motion of gliding dislocations or an internal back stress, d is the grain size, k is the Hall–Petch slope, which reflects the resistance of grain boundary to slip transfer. The abundant TiC and Nd 2 O 3 particles distributed uniformly in the alloy matrix result to the refinement of titanium matrix’s grain size, which may be beneficial to improve the compressive strength. In addition, the strengthening behaviors of the composite may be resulted from the dispersion strengthening of the finer Nd 2 O 3 crystallites dispersed in the eutectic cells and Ti matrix of the composites. From the microstructure of the composites, the grain size of TiC and Nd 2 O 3 particles becomes obviously bigger with the increase of the Nd content. The fine grains are advantage to improve the strength of composites [8,28] . Ma et al. [28] suggest that (TiB + TiC)/Ti composite has higher compressive strength because of the smaller reinforcements, as the strength of the composites generally increases with decreasing size of the reinforcements. Compared with the other composites, the finer reinforcements were observed in the composite reinforced by 10 wt.%TiC and 8 wt.%Nd 2 O 3 particles, which are helpful for the higher compressive strength. 4 Conclusion (TiC + Nd 2 O 3 )/Ti–4.5 wt.%Si composites were in situ synthesized by a non-consumable arc-melting technology from the raw materials of Ti, Si, Nd, SiO 2 , and C. The composites contain four phases: TiC, Nd 2 O 3 , Ti 5 Si 3 and Ti. Reinforcements TiC and Nd 2 O 3 are well distributed in Ti–4.5 wt.%Si alloy matrix, and the morphologies exhibit near-equiaxed and dendritic shapes. Moreover, the abundant fine Nd 2 O 3 particles are found in the network Ti + Ti 5 Si 3 eutectic cells and Ti matrix of the composites. Compared to the unreinforced Ti–4.5 wt.%Si alloy, the hardness and compressive strength of the composites were greatly improved due to the in situ formation of TiC and Nd 2 O 3 particles. At constant TiC content of 10 wt.% in the composites, the hardness is enhanced with the increasing Nd 2 O 3 content from 8 wt.% to 13 wt.%, but the highest compressive strength appear in the 8 wt.% Nd 2 O 3 particles reinforced composite. Acknowledgments This work was financially supported by Program for Changjiang Scholars and the Innovative Research Team in University. References [1] H. Choe S. Abkowitz S.M. Abkowitz D.C. Dunand Mechanical properties of Ti–W alloys reinforced with TiC particles Mater Sci Eng A 485 2008 703 710 [2] Y. Okazaki E. Gotoh Comparison of metal release from various metallic biomaterials in vitro Biomaterials 26 2005 11 21 [3] B. Yang G.X. Chen J.S. Zhang Effect of Ti/C additions on the formation of Al 3 Ti of in situ TiC/Al composites Mater Des 22 2001 645 650 [4] J.L. Li D.L. Jiang S.H. Tan Microstructure and mechanical properties of in situ produced Ti 5 Si 3 /TiC nanocomposites J Eur Ceram Soc 22 2002 551 558 [5] D. Vojtěch B. Bártová T. Kubatίk High temperature oxidation of titanium–silicon alloys Mater Sci Eng A 361 2003 50 57 [6] A.N. Enyashin A.L. Ivanovskii Structural, cohesive and electronic properties of Ti 5 Si 3 nanotubes Physica E 41 2009 1217 1221 [7] C.L. Yeh C.C. Hsu An experimental study on Ti 5 Si 3 formation by combustion synthesis in self-propagating mode J Alloys Compd 395 2005 53 58 [8] S.C. Tjong Z.Y. Ma Microstructural and mechanical characteristics of in situ metal matrix composites Mater Sci Eng R 29 2000 49 113 [9] S.C. Tjong Y.W. Mai Processing-structure-property aspects of particulate- and whisker-reinforced titanium matrix composites Compos Sci Technol 68 2008 583 601 [10] C.L. Yeh R.F. Li Formation of TiAl/Ti 5 Si 3 and TiAl/Al 2 O 3 in situ composites by combustion synthesis Intermetallics 16 2008 64 70 [11] D. Hu M.H. Loretto Microstructural characterization of a gas atomized Ti–6Al–4V–TiC composite Scripta Metall Mater 31 1994 543 548 [12] R. Banerjee A. Genc D. Hill P.C. Collins H.L. Fraser Nanoscale TiB precipitates in laser-deposited Ti–matrix composites Scripta Mater 53 2005 1433 1437 [13] S. Ranganath M. Vijayakumar J. Subrahmanyan Combustion-assisted synthesis of Ti–TiB–TiC composite via the casting route Mater Sci Eng A 149 1992 253 257 [14] D.R. Ni L. Geng J. Zhang Z.Z. Zheng Fabrication and tensile properties of in situ TiB w and TiC p hybrid-reinforced titanium matrix composites based on Ti–B 4 C–C Mater Sci Eng A 478 2008 291 296 [15] G.J. Zhang M. Ando J.F. Yang T. Ohji S. Kanzaki Boron carbide and nitride as reactants for in situ synthesis of boride-containing ceramic composites J Eur Ceram Soc 24 2004 171 178 [16] W.J. Lu D. Zhang X.N. Zhang R.J. Wu T. Sakata H. Mori Microstructural characterization of TiC in in situ synthesized titanium matrix composites prepared by common casting technique J Alloys Compd 327 2001 248 252 [17] J.Q. Lu J.N. Qin W.J. Lu Y. Liu J.J. Gu D. Zhang In situ preparation of (TiB + TiC + Nd 2 O 3 )/Ti composites by powder metallurgy J Alloys Compd 469 2009 116 122 [18] G.P. Li D. Li Y.Y. Liu Z.Q. Hu Interaction between Nd-rich phase particles and liquid–solid interface in as-cast Ti–5Al–4Sn–2Zr–1Mo–0.25Si–1Nd titanium alloy Scripta Metall Mater 33 1995 547 551 [19] O. Knacke O. Kubascheswski R. Hesselman Thermochemical properties of inorganic substance 2nd ed. 2003 Springer Berlin p. 209, 1180, 1190, 1480, 1505, 1519, 1666, 1674 [20] W.J. Lu L. Xiao D. Xu J.N. Qin D. Zhang Microstructural characterization of Y 2 O 3 in in situ synthesized titanium matrix composites J Alloys Compd 433 2007 140 146 [21] W.J. Lu D. Zhang R.J. Wu H. Mori Solidification paths and reinforcement morphologies in melt-processed (TiB + TiC)/Ti in situ composites Metall Mater Trans A 33 2002 3055 3063 [22] J.L. Murray Binary alloy phase diagrams 2nd ed. 1991 ASM International Ohio Materials Park (OH) p. 2817–19 [23] Y. Chen Y.C. Wu F.W. Yu J.L. Chen Microstructure and mechanical properties of tungsten composites co-strengthened by dispersed TiC and La 2 O 3 particles Int J Refract Met H 26 2008 525 529 [24] L.J. Huang L. Geng A.B. Li F.Y. Yang H.X. Peng In situ TiB w /Ti–6Al–4V composites with novel reinforcement architecture fabricated by reaction hot pressing Scripta Mater 60 2009 996 999 [25] D.G. Zhao X.F. Liu Y.C. Pan X.F. Bian X.J. Liu Microstructure and mechanical properties of in situ synthesized (TiB 2 + Al 2 O 3 )/Al–Cu composites J Mater Process Tech 189 2007 237 241 [26] Y.T. Zhao S.L. Zhang G. Chen X.N. Cheng C.Q. Wang In situ (Al 2 O 3 + Al 3 Zr) np /Al nanocomposites synthesized by magneto-chemical melt reaction Compos Sci Technol 68 2008 1463 1470 [27] D.J. Lloyd Particle reinforced aluminium and magnesium matrix composites Int Mater Rev 39 1994 1 23 [28] Z.Y. Ma S.C. Tjong L. Gen In situ Ti–TiB metal-matrix composite prepared by a reactive pressing process Scripta Mater 42 2000 367 373