EFFECTS OF GROWTH RATE ON MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Ti-43Al-3Si ALLOY WITH A SEED TECHNIQUE

Luo Wenzhong,Shen Jun,Li Qinglin,Man Weiwei,Zheng Xunqiang,Liu Lin,Fu Hengzhi

DOI: https://doi.org/10.3321/j.issn:0412-1961.2006.12.002

IF: 1.797

2006-01-01

ACTA METALLURGICA SINICA

Abstract:Directional solidification (DS) of Ti-43Al-3Si alloy with a polycrystalline seed has been studied under the conditions of different growth rates. DS ingots with fully lamellar microstructure parallel to longitudinal axis (DS direction) were successfully obtained at a low growth rate of 60 mm/h. Increasing further the growth rate, the orientation of lamellar microstructure was no longer parallel to the DS direction and an angle of about 45 or 90 appeared between lamellar orientation and DS direction because of the variations of constitutional undercooling and temperature gradient. The distance between the transition point and the seed decreased with the increase of growth rate. Experiments also showed that the seeding process easily failed if the convection caused by electromagnetic stir was strong enough.