Facile Sonochemical Synthesis of Cepo4 : Tb/Lapo4 Core/Shell Nanorods with Highly Improved Photoluminescent Properties

Ling Zhu,Xiaoming Liu,Xiangdong Liu,Qin Li,Jiayan Li,Siyuan Zhang,Jian Meng,Xueqiang Cao
DOI: https://doi.org/10.1088/0957-4484/17/16/036
IF: 3.5
2006-01-01
Nanotechnology
Abstract:A simple, efficient and quick method has been established for the synthesis of CePO4:Tb nanorods and CePO4:Tb/LaPO4 core/shell nanorods via ultrasound irradiation of inorganic salt aqueous solution under ambient conditions for 2 h. The as-prepared products were characterized by means of powder x-ray diffraction (PXRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction ( SAED), x-ray photoelectron spectroscopy (XPS), photoluminescence (PL) spectra and lifetimes. TEM micrographs show that all of the as-prepared cerium phosphate products have rod-like shape, and have a relatively high degree of crystallinity and uniformity. HRTEM micrographs and SAED results prove that these nanorods are single crystalline in nature. The emission intensity and lifetime of the CePO4:Tb/LaPO4 core/shell nanorods increased significantly with respect to those of CePO4: Tb core nanorods under the same conditions. A substantial reduction in reaction time as well as reaction temperature is observed compared with the hydrothermal process.
What problem does this paper attempt to address?