Pervaporation dehydration of an isopropanol aqueous solution using microporous TiO 2 -SiO 2 -OCL (Organic chelating Ligand) composite membranes prepared under different firing conditions
Takaya Fujiki,Megumi Kaji,Yuuya Tamamizu,Ryuuki Yasunari,Keizo Nakagawa,Tooru Kitagawa,Yasunao Okamoto,Atsushi Matsuoka,Eiji Kamio,Hideto Matsuyama,Tomohisa Yoshioka
DOI: https://doi.org/10.1016/j.seppur.2023.126249
IF: 8.6
2024-01-26
Separation and Purification Technology
Abstract:Microporous TiO 2 -SiO 2 composite membranes intended for use in the pervaporation dehydration of a water/isopropanol mixture were prepared via the sol–gel method using acetylacetone (ACA) as an organic chelating ligand (OCL). TiO 2 -SiO 2 -ACA sols were prepared by using titanium (IV) propoxide (TiTP), an alkoxide of Ti, tetraorthoethylsilicate (TEOS), an alkoxide of Si, and ACA, as a composite of TiO 2 and SiO 2 with coordinating OCL to Ti. The dried gels were fired at 300 °C under N 2 or at 500 °C under air, and were analyzed via FT-IR. Both powders had Ti-O-Si bonds, however, OCL in the powder fired at 500 °C in air has decomposed and removed. The TiO 2 -SiO 2 -ACA sols were applied to alumina plates and fired at either 300 °C under N 2 or at 500 °C under air to check the water-contact angle, which indicated that the OCL was retained on the plates fired at 300 °C under N 2 and were more hydrophobic than when fired at 500 °C under air. TiO 2 -SiO 2 -ACA composite membranes were fabricated by coating either the TiO 2 -SiO 2 -ACA sol layer fired at 300 °C under N 2 or that fired at 500 °C under air onto a TiO 2 -SiO 2 intermediate layer with an α-alumina support. The pore sizes of both membranes were estimated via the NKP method for single-gas permeance at 200 °C. The mean pore sizes of the membranes fired under N 2 at 300 °C and under air at 500 °C were 0.47 nm and 0.68 nm, respectively, which suggested the possibility of pore size control via firing conditions. Pervaporation tests of the TiO 2 -SiO 2 -ACA composite membranes in a water/isopropanol mixture (IPA: 90 wt%) showed that the membranes fired under air at 500 °C and under N 2 at 300 °C had values for permeation flux of 0.90 and 0.13 kg/(m 2 h) and separation factors of 667 and 98 at 50 °C, respectively. The higher permeation flux of the membrane fired under air at 500 °C was due to the influence of a larger pore size as well as to a more hydrophilic surface. On the other hand, the separation factor was also higher for the membrane fired under air at 500 °C, because the hydrophilic surface facilitated water permeation. These results indicate the possibility of using firing conditions to control both the pore size and the surface properties of microporous TiO 2 -SiO 2 -ACA composite membranes for use in PV separation.
engineering, chemical