Abstract:Polymer foams are in industrial use for several decades. More recently, non-polar polymer foams were found to be piezoelectric (so-called piezoelectrets) after internal electrical charging of the cavities. So far, few studies have been carried out on the electrical-insulation properties of polymer foams. Here, we compare the piezoelectric and the DC-voltage electrical-insulation properties of cellular polypropylene (PP) foams. Their cavity microstructure can be adjusted via inflation in high-pressure nitrogen gas in combination with a subsequent thermal treatment. While inflation is effective for improving the piezoelectricity, it is detrimental for the electrical-insulation properties. The original cellular PP foam shows a breakdown strength of approximately 230 MV/m, within the same range as that of solid PP. The breakdown strength decreases with increasing degree of inflation, and the dependence on the foam thickness follows an inverse power law with an exponent of 1.2. Nevertheless, up to a thickness of 140 mu m (3.5 times the original thickness), the breakdown strength of cellular-foam PP films is at least 7 times that of an air gap with the same thickness. In addition, the influence of high temperatures and high humidities on the piezoelectricity and the breakdown strength of cellular PP was studied. It was found that the piezoelectric d(33) coefficient decays rapidly already at 70 degrees C, while the breakdown strength slightly increases during storage at 70 or 90 degrees C. Under a relative humidity of 95%, the breakdown strength increases with storage time, while the piezoelectric d(33) coefficient slightly decreases.

Piezoelectricity of Single-and Multi-Layer Cellular Polypropylene Film Electrets

The Piezoelectricity of Heat-Expanded PP Cellular Electret

Influences of Pressure Treatment and Charging Method on the Piezoelectricity of Cellular Polypropylene Film

The Piezoelectricity of P(Vdf-Tfe-Hfp)/Ptfe Double-Layer Electret Films

Analysis and development of a ferroelectret cellular PP film

Light Emission from Cellular Polypropylene Ferroelectrets under High Electric Fields and Its Correlation with Piezoelectricity

Influence of Charging Parameters on Piezoelectricity for Cellular PP Film Electrets

Cellular Polypropylene Foam Films As DC Voltage Insulation and As Piezoelectrets - A Comparison

The Piezoresistance of a Device with Polyphenylenevinylene Derivative PSS-PPV Film

Ultralight and sensitive ferroelectret films with a human skin-like texture

Treatment with Orthophosphoric Acid Enhances the Thermal Stability of the Piezoelectricity in Low-Density Polyethylene Ferroelectrets

Polyethylene-naphthalate (PEN) Ferroelectrets: Cellular Structure, Piezoelectricity and Thermal Stability

Influence of Heat Treatment Temperature after the Pressure Expansion on the Electromechanical Properties of Cellular Polypropylene Electret

Piezoelectric Properties and Charge Dynamics in Poly(vinylidene Fluoride-Hexafluoropropylene) Copolymer Films with Different Content of HEP

Influence of thermal treatment on the electrical and electromechanical properties of Cellular Polypropylene ferroelectrets

Thermal Stability of Piezoelectricity for Porous Polytetrafluoroethylene Electret Film

Piezoelectric Properties of PVDF Modified 3-3 Type Cement-Based Piezoelectric Composites

Piezoelectric Activity of PFA/Porous PTFE/PFA Sandwich-structure Compound Film

A 3D-printed, alternatively tilt-polarized PVDF-TrFE polymer with enhanced piezoelectric effect for self-powered sensor application

Induced Polarization Imparts Piezoelectricity in Non-Crystalline Polymer Films

In-situ Polarization Enhanced Piezoelectric Property of Polyvinylidene Fluoride-Trifluoroethylene Films