The Effect of Fe and Cr on the Microstructure Evolution and Mechanical Properties of GH2107 Superalloy during Long-Term Aging
Yifu Jiang,Shuang Gao,Xiaowei Yin,Jintao Liu,Xuezhi Qin,Lanzhang Zhou,Lin Wang,Qun Zhao,Jun Liu
DOI: https://doi.org/10.1007/s11665-023-08038-6
IF: 2.3
2023-03-12
Journal of Materials Engineering and Performance
Abstract:The effects of alloying elements on the microstructure evolution and properties of GH2107 superalloy during long-term aging are investigated by optical microscope, scanning electron microscope, and transmission electron microscope. The results indicate that the microstructure of the alloy becomes unstable with the prolongation of aging time. Cr element promotes the precipitation of M 23 C 6 carbides at grain boundaries, and Fe element inhibits the precipitation and growth of M 23 C 6 carbides at high temperature. At the same time, high Fe promotes the growth of γ' phase and the precipitation of TCP phase, which has a certain influence on the plasticity and strength of the alloy. The yield strength of alloy1 (15.41% Cr, 35.3% Fe) and alloy2 (15.08% Cr, 40.1% Fe) decreases with the increase in aging time. However, for alloy3 with high Fe content, the yield strength increases suddenly at 3000 h aging time due to the improving effect of solid solution strengthening. In addition, the dislocation movement mechanism of GH2107 alloy was studied, and Orowan bypass mechanism is more likely to occur in alloys with high Fe content.
materials science, multidisciplinary