Abstract:Three-dimensional braided carbon fiber/epoxy resin composites are significant structural materials in the fields of astronauts and aeronautics. The effect of the process and test parameters on the mechanical properties was studied in this paper. Optical microscope and field emission gun scanning electron microscope (SEM) were used to analyze the macro- and micro-fracture morphology. The fracture morphology of the three-dimensional braided carbon fiber/epoxy resin composites was varied under different loading rates. The results indicate that the mechanical properties can be significantly affected by the parameters of braiding. By decreasing the braided angle the elastic modulo E and ultimate tensile strength showed an obvious increase. The fracture process depends on stress transfer behavior. The fracture characteristic was brittle, which originated from plastic constraint at the fiber. Fiber fracture was caused by a defect on the surface of the carbon fiber in low loading rate. As the explosive impact test was carried out in a special attachment, superior energy absorption capability and damage tolerance were found. Due to high bursting pressure a surface ablation region was formed and a notch was observed in the region. The fibers in the surface ablation region were sheared off and pulled out. The fracture of fiber was scarcely related to any fiber defects in this region. There was a damage region under the ablation layer. Fracture morphology revealed that the epoxy area between fibers showed crack growth traces, which looked like a river pattern. The river pattern is the sign of brittle fracture and the direction of the river pattern is toward the direction of crack spreading. The fracture process showed that damage formation were fiber sheared off and epoxy flaked off under the ablation region. The propagation path of the macro-crack is mainly in the braided sheaf and along the sheaf interface under the ablation region.

Flexural Behavior of 3DC/C Composites

Compressive testing and failure analysis of three-dimensionally reinforced carbon/carbon composites

Mechanical Behaviors of the Three-Dimensional Woven Carbon/carbon Composite Materials under Biaxial Compression

Experimental and numerical study of in-plane compressive properties and failure of 3D six-directional braided composites with large braiding angle

Experiment investigation on biaxial tensile strength of 3D in-plane braided C/C composites

Mechanical Properties Analysis of Quasi-3D C/C Composites

Study on in-plane compression properties and numerical modeling of three dimensional five-directional braided composites

Experimental study on tension and compression mechanical property of 3D fine woven punctured C/C composites

Compressive properties and failure mechanism of 3D C/C composites

Study on flexural properties and failure mechanism of fibre/fabric reinforced composite laminates

Experimental and numerical research on flexural behavior of fiber metal laminate sandwich composite structures with 3D woven hollow integrated core

Study on Tensile and Compressive Properties and Size Effect of 3D Fine Woven Punctured C/C Composites

Experimental Investigation on the Mechanical Behaviour of 3D Carbon/carbon Composites under Biaxial Compression

Transverse bending fatigue behaviors and failure mechanisms of 3D five-directional braided composites at different temperatures

Mechanical properties of a novel Tri-directional carbon-flax-aramid fiber reinforced composite

Experimental Investigation on Compressive Properties for 3d Four-Directional Braided Composites

Structural influences of two-dimensional and three-dimensional carbon/epoxy composites on mode I fracture toughness behaviors with rate effects on damage evolution

Effect of braiding angle on bending properties of 3D-Cf/6061Al composites

Investigation of parameterized braiding parameters and loading directions on compressive behavior and failure mechanism of 3D four-directional braided composites

The Smart Behavior of Cement-Based Composite Containing Carbon Fibers under Three-Point-bending Load

Dynamic damage and fracture mechanism of three-dimensional braided carbon fiber/epoxy resin composites