Preparation of perpendicularly oriented FePt films by annealing in a magnetic field

Xiaoyuan Zhan,Yousong Gu,Xiaolan Zheng,Yue Zhang

2006-01-01

Abstract:FePt films have been deposited onto natural-oxidized Si(100) single crystal substrate by magnetron sputtering, the structural and magnetic properties were investigated using X-ray diffractometer (XRD) and vibrating sample magnetometer (VSM). A magnetic field from zero up to 10000 kA/m was applied in perpendicular direction to the film during annealing, in order to make the easy axes orienting perpendicular to the film. X-ray diffraction showed that the FePt undergo a order-disorder-order transition, the coercivity of the FePt film decrease first, and then increases with external magnetic field, but the ordering parameter S along the perpendicular direction increase all the way. The coercivity of the FePt film was 83 kA/m while the ordering parameter (S) was 0.89 after annealing in a magnetic field of 10000 kA/m.