Abstract:Indium hydroxide (In(OH)(3)) nanorods and Sn-doped indium oxyhydroxide (InOOH) nanoparticles were synthesized through the hydrothermal method in an aqueous solution. Sodium hydroxide (NaOH) was introduced to adjust the pH value, and sodium acetate (CH3COONa) was employed as the inducer to accelerate the growth along the preferential orientation. Cubic In(OH)(3) was synthesized at pH values ranging from 4.0 to 8.0. In(OH)(3) nuclei grows in the direction {100} into nanorods observed from lattice fringes with an interplanar spacing of about 0.403 nm. The SAED pattern of In(OH)(3) nanorods indicates the rodlike nanocrystal is a single crystal which matches well with the characteristic peaks of cubic In(OH)(3) XRD patterns. The FTIR spectrum signifies the absorption of CH3COO- onto the surface of In(OH)(3) nanorods, which accelerate the growth along the direction {100}. Due to the inhibition effect of OH-, In(OH)(3) particles with a smaller aspect ratio and In2O3 particles with a smaller crystal size were synthesized with the increase of pH values. At a high hydrothermal temperature, cubic In(OH)(3) transformed into orthorhombic InOOH owing to the dopant of Sn with a size smaller than In3+ and r(Sn4+)/r(O2-) = 0.58. The lattice fringes and SAED patterns of InOOH and hexagonal In2O3 nanoparticles were determined. It was also observed that the average size increased from 27 to 46 nm when Sn doping content increased from 2% to 10%. The sensors based on the Sn-doped In2O3 nanoparticles showed a fast (6-7 s) and high response (R-a/R-g = 8.9) to 100 ppm acetone at an operating temperature of 280 degrees C. This work provides a preliminary investigation into the effect of sodium acetate and Sn on the growth of In(OH)(3) nuclei.

Anisotropic Growth of In(OH)3 Nanocubes to Nanorods and Nanosheets Via a Solution-Based Seed Method

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Growth of Tin Oxide Nanorods Induced by Nanocube-Oriented Coalescence Mechanism

Shape Evolution Of Pb (Zr,Ti)O-3 Nanocrystals Under Hydrothermal Conditions

Size-Controllable Growth of Single Crystal In(OH)3 and In2O3 Nanocubes

Anion-induced morphological regulation of In(OH) 3 nanostructures and their conversion into porous In 2O 3 derivatives

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Tunable Synthesis of Various Hierarchical Structures of In(Oh)(3) and In2o3 Assembled by Nanocubes

Facile Synthesis of Single-Crystal Tin Oxide Nanorods with Tunable Dimensions Via Hydrothermal Process

Preparation of In(Oh)(3) Nanorods and Nanocubes and the Effect on In2o3 Particle Size in the Microreactor

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

Tunable synthesis of In<sub>2</sub>O<sub>3</sub> nanowires, nanoarrows and nanorods

Biomolecule-assisted synthesis of In(OH)3 hollow spherical nanostructures constructed with well-aligned nanocubes and their conversion into C-In2O3

Preparation of In(OH)(3) and In2O3 Nanorods Through a Novel Hydrothermal Method and the Effect of Sn Dopant on Crystal Structures

Solution-Phase Tailored Growth of Nb3o7(Oh) Thin Films

Shape-Controllable Synthesis of Indium Oxide Structures: Nanopyramids and Nanorods

Help nanorods "stand" on microsubstrate to form hierarchical ZnO nanorod-nanosheet architectures

Hydrothermal Growth and Morphology Modification of Β-Nis Three-Dimensional Flowerlike Architectures

Size-controllable Growth of ZnO Nanorods on Si Substrate

Growth Of Zno Crystals With Branched Spindles And Prismatic Whiskers From Zn-3(Oh)(2)V2o7 Center Dot H2o Nanosheets By A Hydrothermal Route