Synthesis And Characterization Of Neodymium Hydroxide And Oxide Nanowires

Px Huang,B He,F Wu,Gl Pan,Xp Gao
2006-01-01
Chinese journal of inorganic chemistry
Abstract:Hexagonal neodymium hydroxide nanowires about 20 similar to 40 nm in diameter and up to several micrometers in length were prepared through a hydrothermal reaction in alkaline solution at 180 T for 45 h. The obtained products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was demonstrated that the hydrothermal temperature, alkaline concentration and alkaline reagents (KOH, NaOH and LiOH) were all had their own effects on the morphology, aspect ratio and crystallinity of the final products. The increase in the hydrothermal temperature and alkaline concentration led to the preferable growth of neodymium hydroxide nanowires. At the same hydrothermal temperature and alkaline concentration, neodymium hydroxide nanowires prepared using the NaOH solution had a better purity and higher aspect ratio. After the calcination of neodynnum hydroxide nanowires at 500 degrees C in air, the C-type neodynnum oxide nanowires with bcc structure were obtained.
What problem does this paper attempt to address?