Abstract:Using tert-butyl peroxy-2-ethyl hexanoate (TPRO) as initiator,the vinyl acetate (VAc) bulk grafting polymerization in the presence of polyethylene glycol (PEG) to get the PEG-g-PVAc was studied. The time evolution of polymerization rate,grafting ratio,grafting efficiency and molecular weight of the grafted copolymer were investigated respectively for various weight ratios of VAc to PEG. The results show that,with increasing VAc?PEG ratio,the polymerization rate and final conversion ratio are both enhanced,and an observable automatic acceleration phenomenon begins to appear. The overall reaction rate coefficient K increases with reaction time at higher VAc:PEG ratio,while a tendency of decrease of K with reaction time at lower VAc:PEG ratio was observed. At almost all VAc:PEG ratios,the grafting ratio was found to increase linearly with the conversion ratio,and the grafting efficiency keeps almost unchanged throughout the whole conversion. The grafting ratio is in proportion to VAc:PEG ratio,while the grafting efficiency is generally very high and can reach above 95% at low VAc?PEG ratio. Although the PEG grafted efficiency increases with both monomer consumption and rising VAc?PEG ratio,the overall PEG grafted efficiency is low,it indicates that a great amount of undrafted PEG exists. The phenomenon of high VAc grafting efficiency accompanying with low PEG grafted efficiency indicates that the 'Graft From' polymerization system may undergo a 'Graft Onto' mechanism. According to the definition,the PEG-g-PVAc number-average molecular weights were calculated,and the results show that the number-average molecular weights reduce at first with the increase of conversion ratio,and then approach to a constant; the higher the VAc?PEG ratio,the higher the number-average molecular weight. Via GPC analysis and PVAc universal calibration,the PDI (polydispersity index) of the grafted copolymer was determined to be between 1.5 ～ 2.5 and it aggrandizes with the increase of VAc concentration and conversion. It might be considered that,all these phenomena are related to the gel effect in the polymerization system.

Characteristic Scaling Exponent (ν) of Polyethylenglycol(PEG) at the Air-aqueous Solution Interface

Densities and Viscosities of Polyethylene Glycol + Salt + Water Systems at 20 .Degree.c

Kinetic Study of Vinyl Acetate Graft Polymerization on PEG

Preparation and characterization of polyethylene glycol/poly(L-lactic acid) blends

Effects of Poly(ethylene Glycol) Molecular Weight on the Stability of Surfactant-Free Emulsion Polymerization System Consisting of Styrene and Methyl Methacrylate

Toughness Enhancement and Stick–Slip Tearing of Double-Network Hydrogels in Poly(ethylene Glycol) Solution

Scaling Property of Polymer Liquid-Crystal Langmuir Monolayers

Effects of the Extractant on the Hydrophilicity and Performance of High-Density Polyethylene/Polyethylene-B-Poly(Ethylene Glycol) Blend Membranes Prepared Via A Thermally Induced Phase Separation Process

Effect of PEG Additives on Properties and Morphologies of Polyetherimide Membranes Prepared by Phase Inversion

Polyacrylonitrile Membranes Via Thermally Induced Phase Separation: Effects of Polyethylene Glycol with Different Molecular Weights

VISCOMETRIC STUDIES ON THE INTERACTION BETWEEN POLYACRYLAMIDE AND POLY(ETHYLENE GLYCOL) IN WATER

Excess properties, spectral analyses and computational chemistry of the binary mixture of polyethylene glycol 200 + 1,3-propanediamine

Thermal and Physical Characterization of PEG Phase Change Materials Enhanced by Carbon-Based Nanoparticles

Intermolecular Interaction in Aqueous Solution of Binary Blends of Poly(Acrylamide) and Poly(Ethylene Glycol)

Analysis of interfacial phenomena of aqueous solutions of polyethylene oxide and polyethylene glycol flowing in hydrophilic and hydrophobic capillary viscometers

Excess Properties, Spectral Analyses, and CO2 Capture Performance of N-methyldiethanolamine + Polyethylene Glycol 300 Binary System

Molecular dynamics coupled with experimental study of the effects of polyethylene glycol on the structure and antifouling properties of polyethersulfone membranes

Effect of PEG Additive on Formation of PEK-C Microporous Membrane

Effect of PEG Additives on Properties and Morphologies of Membranes Prepared from Poly(2,6‐dimethyl‐1,4‐phenylene Oxide) by Benzyl Bromination and in Situ Amination

Tuning the water intrinsic permeability of PEGDA hydrogel membranes by adding free PEG chains of varying molar masses