Photoresponsive Character in Double-Doped La2/3(Ca2/3Sr1/3)1/3MnO3 Thin Film

YC Wang,R Ren,CL Chen,DA Ren,KX Jin,X Yuan,SG Zhao,ZM Song
DOI: https://doi.org/10.1139/p05-033
2005-01-01
Canadian Journal of Physics
Abstract:A Ca, Sr double-doped La-2/3(Ca2/3Sr1/3)(1/3)MnO3 thin film with a thickness of about 60 nm was deposited on (100) LaAlO3 substrates using the RF magnetron sputtering method from the bulk compound prepared using the solid-state reaction method. The experimental results show that a phase transition from the ferromagnetic metallic state to the paramagnetic insulating state occurs at 341 K (near to T-p, the highest peak temperature). The R-T curve deviation of the thin film with the application of CW laser is dramatic in the low-temperature range and Delta R/R is positive. At 276 K, the Delta R/R reaches the maximum, about 41 %, and the temperature of the photo-induced resistance maximum of this double-doped thin film appears near to room temperature range, which offers a new method for the application of CMR photo-electric devices.
What problem does this paper attempt to address?