Biocompatibility of swelling polyethylene compound biomembrane for preventing peridural adhesion

Bo-jun Dai,Xiao-jian Ye,Hong Lü,Hai-long He,Jia-shun Li,Lian-shun Jia

DOI: https://doi.org/10.3321/j.issn:1673-8225.2005.02.034

2005-01-01

Abstract:Aim: To evaluate the in vitro biocompatibility of swelling polyethylene compound biomembrane, a self-made absorbable adhesive material in medicine for the prevention of epidural adhesion. Methods: The experiment was completed in the laboratory for Department of Hepatobiliary Surgery, Second Military Medical University of Chinese PLA from March 2003 to August 2003. The cytotoxicity test, hemolytic test and acute whole body intoxication toxicity test were performed with standard method. Results: 1 The fibroblasts of L-929 mice were in good morphology and proliferation after treated with swelling polyethylene compound biomembrance extract solution. At 2, 4 and 7 days, the absorbance (A) values were 0.552 ± 0.044, 0.783 ± 0.040 and 1.198 ± 0.052 respectively in polyethylene compound group, significantly different from those in the positive control group(0.347 ± 0.025, 0.446 ± 0.018 and 0.565 ± 0.025 respectively) (t = 26.47 to 31.12, P < 0.01). The relative proliferation rate was higher than 100%, and the toxicity gradation of the material was 0. 2 The hemolysis rate was 2.21% (< 5%), which was in accordance with the standard of hemolytic test. 3 No acute whole body intoxication reaction was found. The body mass of the animals were increased by (1.77 ± 0.42), (2.57 ± 0.39) and (3.30 ± 0.43) g respectively in polyethylene compound group at 24, 48 and 72 hours, and by(-2.79 ± 0.23), (-3.83 ± 0.35) and(-3.89 ± 0.34) g in positive control group, so there were significant difference between the two groups(t = 58.34 to 87.12, P < 0.01). Conclusion: The swelling polyethylene compound biomembrane has good biocompatibility.