Abstract:The effect of Al substitution for Fe on crystal structure, magnetostriction and spontaneous magnetostriction, anisotropy and spin reorientation of a series of polycrystalline Tb0.3Dy0.7(Fe1−xAlx)1.95 alloys (x = 0, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, 0.35) at room temperature and 77 K was investigated systematically. It was found that the primary phase of Tb0.3Dy0.7(Fe1−xAlx)1.95 is the MgCu2-type cubic Laves phase structure when x < 0.4 and the lattice constant a of Tb0.3Dy0.7(Fe1−xAlx)1.95 increases approximately and monotonically with the increase of x. The substitution of Al leads to the fact that the magnetostriction λ inceases slightly in a low magnetic field (H ⩽ 40 kA/m), but decreases sharply and is easily close to saturation in a high applied field as x increases, showing that a small amount of Al substitution is beneficial to a decrease in the magnetocrystalline anisotropy. It was also found that the spontaneous magnetostriction λ111 decreases greatly with x increasing. The analysis of the Mössbauer spectra indicated that the easy magnetization direction in the {110} plane deviates slightly from the main axis of symmetry with the changes of composition and temperature, namely spin reorientation. A small amount of non-magnetic phase exists for x = 0.15 in Tb0.3Dy0.7(Fe1−xAlx)1.95 alloys and the alloys become paramagnetic for x > 0.15 at room temperature, but at 77 K the alloys still remain magnetic phase even for x = 0.2. At room temperature and 77 K, the hyperfine field decreases and the isomer shifts increase with Al concentration increasing.

Solidification Characteristics of Tb0.27Dy0.73Fex (x=1.8, 1.95) Alloys During the Directional Solidification

Interface shape and preferred orientation in the directional solidification Tb0.27Dy0.73Fe19.5 alloy

Solidification Behavior of Dy-Tb-Fe Alloys through Experimental Study and Thermodynamic Calculation

Solidification of R-Fe Alloy in Magnetic Field

Vertical sections of Tb0.15Ho0.85Fey-Tb0.3Dy0.7Fey（y=1.85, 1.9, 2.0） in Tb-Dy-Ho-Fe system

The Effect of Overheating Treatment on the Microstructure of TbDyfe Alloys

-orientation growth of Tb-Dy-Fe alloys induced by high magnetic fields during directional solidification

Preparation of Terfenol-D with Precise 〈110〉 Orientation and Observation of the Oriented Growth Crystal Morphology

The Directional Solidification, Microstructural Characterization and Deformation Behavior of Β-Solidifying TiAl Alloy

Structure, Spin Reorientation and Mössbauer Effect Studies of Tb 0.3 Dy 0.7 (fe 1− X Al X ) 1.95 Alloys

Growth of large crystallites of Co37Ni34Al29 ferromagnetic shape memory alloys under super-high temperature gradient directional solidification

Morphology evolution and enhanced magnetostriction of (Fe0.81Ga0.19)99.9Tb0.1 crystals prepared by liquid metal cooling Bridgman directional solidification

Ferromagnetic and Magnetostrictive Properties of Tb0.3Dy0.7(Co1−xFex)2alloys

New smiting and gating technology for TbDyFe alloy bar

Effects of the crystal growth velocity on the crystal orientations and microstructures in an optical image zone melting furnace

Magnetics, Magetostriction, and Spin Reorientation of Tb0.3dy0.6pr0.1(Fe1-Xalx)(1.95) Alloys with Substitution of Fe by Al

Multiscale Influence of Trace Tb Addition on the Magnetostriction and Ductility of 〈100〉 Oriented Directionally Solidified Fe-Ga Crystals

SOLIDIFICATION PHASE SELECTION IN DIRECTION-ALLY SOLIDIFIED Ti–(44%—54%)Al ALLOYS

Microstructure evolution and solidification behaviour of Nb–16Si–22Ti–2Cr–2Al–6Hf alloy processed by directional solidification

Equiaxed to Columnar Transition of Ti46Al8Nb0.5B Intermetallics During Directional Solidification

Effects of substituting Al for Fe on microstructure,magnetostriction and mechanical properties of oriented Tb-Dy-Fe alloy