Abstract:In this work, WMo nanopowders were prepared by sol-gel synthesis combined with hydrogen reduction. The phase distribution of the powders with calcination and reduction at different temperatures was analyzed to figure out the effect of temperature on the reaction process. The calcined powders were further analyzed by thermogravimetric analysis (TGA) and differential thermal analysis (DSC). The phase composition, grain size and powder morphology of the resulted WMo nanoparticles have been characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and transmission electron microscopy (TEM). The precursor calcined at 450 °C consisted of W0.4Mo0.6O3 and MoO3 phases which can be completely reduced to be pure WMo nanopowders with an average grain size of 20–40 nm at a low temperature of 700 °C for 1 h. The grain growth characteristics of the WMo nanopowders were investigated by analyzing the compacts annealed at temperatures ranging from 950 °C to 1400 °C for different time periods. The grain growth mechanism and the activation energy (Qg = 220 ± 21 kJ/mol) of WMo nanoparticles was also obtained.

Hydrothermal Synthesis Of Multielemental Bimetallic Mo1.8w16.2o49 Nanorods

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Selective Synthesis and Characterization of Single-Crystal Silver Molybdate/Tungstate Nanowires by A Hydrothermal Process

A new hydrothermal route for synthesis of molybdenum disulphide nanorods and related nanostructures

Morphology-controlled Synthesis of CdWO_4 Nanocrystals

Synthesis of some transition MWO4 (M: Mn, Fe, Co, Ni, Cu, Zn, Cd) nanostructures by hydrothermal method

Preparation and Characterization of Tungsten-substituted Molybdenum Disulfide Nanorods

Preparation Of Bimetallic Onion-Structured Nano Mo0.9w0.1s2

Hydrothermal Synthesis of MoO3 Nanobelts and Their Electrochemical Characterization

Tungstenic acid induced assembly of hierarchical flower-like MoS2 spheres

General Synthesis of Single‐Crystal Tungstate Nanorods/Nanowires: A Facile, Low‐Temperature Solution Approach

Sol-gel synthesis and characterization of tungsten-molybdenum solid solution nanoparticles

Synthesis of Single-Crystal Bamo2o7 Nanowire Bundles: A General, Low-Temperature Hydrothermal Approach to 1d Molybdenum Oxide-Based Nanostructures

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

General Synthesis and Phase Control of Metal Molybdate Hydrates MMoO4·nH2O (M = Co, Ni, Mn, N = 0, 3/4, 1) Nano/Microcrystals by a Hydrothermal Approach: Magnetic, Photocatalytic, and Electrochemical Properties

Roughness induced wettability amplification of novel copper molybdate-branched CuO nanorod arrays by non-aqueous solution method

Molybdenum Trioxide Nanostructures Prepared by Thermal Oxidization of Molybdenum

Hydrothermal Synthesis and Characterization of Nanorods “Lixv2−δo4−δ·h2o”

A facile hydrothennal route to the large-scale synthesis of CoWO4 nanorods

Hydrothermal Route to Single Crystalline Α-Moo3 Nanobelts and Hierarchical Structures