Gas-phase oxidation of propylene to propylene oxide over modified Ag/TS-1 catalysts

Ruipu Wang,Xinwen Guo,Xiangsheng Wang,Chuanfu Wang,Jingquan Hao

2004-01-01

Abstract:The effects of incorporation of Cu, Pd and La, steam treatment, silylation treatment, as well as washing times of Ag/TS-1 catalyst on its catalytic properties of propylene oxidation using oxygen as an oxidant were investigated at 150°C and atmospheric pressure in a fixed-bed quartz reactor. The catalysts were characterized by UV-Vis, TEM and ICP, respectively. The incorporation of small amount of palladium (Pd) would improve the catalyst stability. Compared with the catalyst of Ag loaded on La impregnated TS-1, the catalyst of Ag loaded on the La deposited TS-1 decreased drastically for its propylene oxide (PO) selectivity, from about 90% to 64%. Steam treatment resulted in detriment to catalyst activity. The silylation of support TS-1 led to the increase of catalyst activity and selectivity. Excessive loading of SiO2 resulted in the decrease of PO selectivity from 98% to 90% as shown by the TEM photos that the Ag particles loaded on the surface of the support forming bigger aggregates. When 2% (mass fraction) SiO2 was loaded, the propylene conversion and the selectivity to PO are 2.1% and 98%, respectively. During the preparation of Ag/TS-1 catalyst, the contents of Ag and K in the catalyst without washing showed the optimum catalytic properties; the propylene conversion and the selectivity to PO were 2.43% and 86.97%, respectively.