Structural and Magnetic Properties of FePt–C Nanocomposite Films

H Wang,FJ Yang,KS Chen,B Zhou,YW Zhang,HS Gu,MF Chiah,WY Cheung,SP Wong
DOI: https://doi.org/10.1088/0256-307x/21/5/052
2004-01-01
Abstract:Nanocomposite FePt–C thin films were prepared by a pulsed filtered vacuum arc deposition technique. The films were characterized by non-Rutherford backscattering spectrometry, x-ray diffraction, and magnetic force microscopy. The dependence of magnetic properties against annealing temperature was studied by using a vibrating sample magnetometer. Both x-ray diffraction and magnetic force microscopy analyses confirmed the formation of nano-crystallites of face-centred-tetragonal phase of FePt in the carbon matrix after annealing at a sufficiently high temperature. For the film with a composition of (Fe0.55Pt0.45)0.78C0.22, the coercivity and the grain size were observed to increase with increasing annealing temperature, up to a value of 3.5 kOe at an annealing temperature of 650 degrees C, and with a grain size about 10.5 nm.
What problem does this paper attempt to address?