Structures and Properties of Dielectrics in Pb(Mg1/3Nb2/3)O3–La(Mg1/2Ti1/2)O3 System

X Hu,XM Chen

DOI: https://doi.org/10.1063/1.1637727

IF: 2.877

2004-01-01

Journal of Applied Physics

Abstract:(1−x) Pb(Mg 1/3 Nb 2/3 ) O 3 –x La(Mg 1/2 Ti 1/2 ) O 3 dielectrics were prepared by a solid-state reaction process and the structures were evaluated together with the dielectric characterization. The pyrochlore-free dielectrics were obtained with increasing La(Mg1/2Ti1/2)O3 content due to the increased electronegativity difference. The 1/2(111) superlattice reflection showed 1:1 ordering on the B site in all compositions. Antiphase tilting of oxygen octahedra and B-site cation displacing appeared at x=0.9. Low loss (tan δ∼10−4) dielectrics with high dielectric constant (36–900) were obtained in the present system, and the good microwave dielectric properties were achieved in the compositions with x⩾0.7. The best combination of microwave dielectric properties was obtained for x=0.9: ε=34, Qf=21 280 GHz, and τf=−60 ppm/°C.