Polylactic acid gel for preventing tendon adhesion after tendon anastomosis

刘立岷,宋跃明,段宏,丁永利,卢冰

DOI: https://doi.org/10.3321/j.issn:1673-8225.2004.26.045

2004-01-01

Abstract:BACKGROUND: Tendon adhesion after tendon anastomosis happens easily,which affects functional recovery. A few materials have been used to prevent adhesion,but there is not yet an ideal material. Recent investigations mostly used solid materials as diaphragm to make tendons move easily.OBJECTIVE: To determine the ability of the polylactic acid gel (PLA-G)in preventing tendon adhesion.DESIGN: A randomized controlled trial was conducted.SETTING and PARTICIPANTS: The experiment was completed in the Department of Laboratory Animal Surgery,West China Hospital,Sichuan University. Sixteen Japanese white rabbits were used in this experiment in either gender(provided by this Department).INTERVENTIONS: The tendons of the soleus muscle of the left hind legs of 16 rabbits were partially separated and the transverse incisions were made over half of their cross seetion. The incision sites were then anastomosed and covered up with the PLA-G. In the control group(the tendons of the soleus muscle of the right hind legs of the rabbits),the tendons were done according to the left and no PLA-G was used at the anastomosis site.MAIN OUTCOME MEASURES: Gross,histological and ultrastructural observations were performed on the tendons and sheaths in the operated parts.week,the PLA-G had good separating function; the tendons and sheaths did not adhere to each other. In the 4th week,the PLA-G began to degrade,but the moving function of the tendons was good. In the 6th and 10th week,there was a little scar in local space,and the tendons grew well in anastomosis and could slide smoothly. While in control groups there was a large proliferative logical observation: in trail groups the arrangement of the tendon fibers at the anastomosis site progressed from irregularly to regularly as time went by; the surface of the tendons was smooth; the fibroblast proliferated inactively. In control groups,the tendon fibers and sheath tissues oonfused without distinct delimitation; a large number of fibroblasts proliferated and collagen secreted.rough surfaced endoplasmic reticulum than the control groups,and less collagen was secreted.CONCLUSION: The PLA-G is a reliable and effective material to reduce tendon adhesion without affecting tendon healing.