Effect of Mould Materials on the As-Cast Microstructures of a Super-High Strength Al Alloy Cast by Low Frequency Electromagnetic Casting

J Dong,XT Liu,ZH Zhao,WP Bao,JZ Cui

DOI: https://doi.org/10.3321/j.issn:0412-1961.2004.02.020

IF: 1.797

2004-01-01

ACTA METALLURGICA SINICA

Abstract:The effect of mould materials on the magnetic intensity in ingots was numerically simulated, then the magnetic intensities without ingots were measured, and some experiments were conducted to study these effects. The results show that during low frequency electromagnetic casting the mould with high electrical resistivity such as titanium alloy can greatly reduce eddy loss of mould, thus increase useful power. At the same condition, when the ingot was cast by titanium alloy mould (high electrical resistivity), the microstructures is uniform and fine, the average grain sizes at the border and center of the ingot are 24 mum and 27 mum respectively, but when the ingot was cast by aluminum alloy mould (low electrical resistivity), the microstructures of both the border and center of the ingot are coarse, their average sizes are 38 mum and 45 mum. Furthermore, the mould with higher electrical resistivity can increase the content of solute elements within grains.