Syntheses and Properties of Poly(Schiff-Base)-Fe2+ Complexes Containing 2,4-Diamino-6-phenyl-s-triazene

ZC Liu,WL Sun,S Liu,ZQ Shen

2004-01-01

Abstract:The synthesis of six novel poly(schiff-base)s, such as PBTGZ, Which is obtained by polycondensation of 2,4-diamino-6-phenyl-s-triazine and 2,2'-diamino-4,4'-bithiazole (DABT) with glyoxal. The polycondensation was processed under acidic condition with the effect of acetic acid. The preparation of two complexes of Fe2+ are described. Their structures were determined by FTIR and H-1-NMR, The values of [eta] were obtained at 30degreesC by using an Ubbelodhe viscomter with capillary diameter of 0.55 mm. The decomposition temperatures of DAPTPA, DAPIPA and DAPA obtained by thermogravimetic analysis were all above 300degreesC, indicating good thermal stability. The temperature dependence of magnetization at an applied field 2.39 x 10(6) A/m and the applied field dependence of magnetization at 5 K for the Fe2+ complexes were measured by PPMS (physical property measurement system). The saturation values of magnetization of PBTPZ-Fe2+ and PBTGZ-Fe2+ were 5.4 Am-2/kg and 2.6 Am-2/kg, and the coercive force of the complexes were 7564 A/m and 75876 A/m, respectively. The "S" shape of magnetic hysteresis loop for PBTPZ-Fe2+ and PBTGZ-Fe2+ and their values of residual magnetization 0.165 Am-2/kg and 0.011 Am-2/kg indicated they were soft magnets. The existence of benzenes ling enlarges the distance of two adjacent Fe2+, ions, which causes the difference of the magnetic proper-ties of the two complexes.