Abstract:Weakly agglomerated nanocrystalline scandia doped tin oxide powders with high surface area (170−220 m2/g) and uniform size (3−4 nm) were synthesized for the first time by a two-step hydrothermal process in the presence of urea, followed by the calcination between 500 and 1200 °C. The structure and texture of the binary oxide system were characterized by thermogravimetry and differential thermal analysis, Brunauer−Emmett−Teller-specific surface area analysis, transmission electron microscopy, X-ray diffraction, Raman spectroscopy, and X-ray photoelectron spectroscopy. A metastable scandium tin oxide solid solution in tetragonal structure was formed for the scandia content lower than 6 mol % as the samples were calcined at 800 °C, and the excess Sc atoms were dispersed at the surface of the crystallites above this limit. The solid solution was metastable, so scandium migrated toward the surface region of the crystallites and produced a second phase of Sc4Sn3O12 during calcining at high temperatures over 1000−1200 °C. In the case of the samples with higher dopant concentration (>15 mol %), the calcination at the temperature between 500 and 800 °C caused the precipitation of Sc2O3, and the calcination over 1000−1200 °C led to the formation of more Sc4Sn3O12. Textural analysis showed that doping an appropriate amount of Sc2O3 into nanosized SnO2 could effectively inhibit the grain growth and stabilize the surface area against high-temperature calcinations below 1000 °C. CO gas-sensing property measurements revealed that the dispersion of Sc at the surfaces of the SnO2 nanocrystallites could improve the CO sensitivity significantly, and the pellet sample with scandia content of 10 mol % sintered at 800 °C showed the best CO gas-sensing property in the operation temperature range of 300−400 °C. On the basis of the structural and textural analysis, the correlation between the structure/texture and the sensitivity to CO for the as-calcined (SnO2)1-x(Sc2O3)x nanocrystallites has been established and explained.

Synthesis Of Crystalline Ato Nanoparticles By Combustion Method

Preparation of Antimony Doped Tin Oxide (ATO) Nanopowders by Hydrothermal Method

Synthesis of Monodispersed Antimony Doped Tin Oxide Nanoparticles and Its Self-Assembly

Chemically Synthesized Sb-Doped SnO 2 Nanoparticles for Supercapacitor Application

The gas-phase formation of tin dioxide nanoparticles in single droplet combustion and flame spray pyrolysis

Unveiling the chemical and morphological features of Sb-SnO2 nanocrystals by the combined use of high-resolution transmission electron microscopy and ab initio surface energy calculations

Nanomaterials Via Solution Combustion Synthesis: a Step Nearer to Controllability

Sb-doped tin oxide nanonets for improved conductivity in transparent conductive coatings

Fine-tuning the Cross-Sectional Architecture of Antimony-doped Tin Oxide Nanofibers As Pt Catalyst Support for Enhanced Oxygen Reduction Activity

Structural, morphological, electrical and optical properties of SnO2 nanoparticles: influence of Sb doping

Amorphous P-Type AlSnO Thin Film by a Combustion Solution Process

Synthesis of Sno2 Nanoparticles Using A Solution Plasma and Their Gas-Sensing Properties

Electrochemical performance of a Sb-doped SnO2 support synthesized by coprecipitation for oxygen reactions

Metastable CoCu2O3 Nanocrystals from Combustion‐Aerosols for Molecular Sensing and Catalysis (Adv. Mater. 47/2024)

Temperature-dependent structural and optical properties of Sb-doped SnO2 nanoparticles and their electrochemical analysis for supercapacitor application

Combustion Synthesis of Tinxc1-X Powders with Ultra Fine Particle Size by Using Titanium Oxide As Dilution

Synthesis, Structure, Texture, and CO Sensing Behavior of Nanocrystalline Tin Oxide Doped with Scandia

Controllable Low-Temperature Hydrothermal Synthesis and Gas-Sensing Investigation of Crystalline SnO 2 Nanoparticles

Effect of Sb Segregation on Conductance and Catalytic Activity at Pt/Sb-Doped SnO2 Interface: A Synergetic Computational and Experimental Study

A Simple Method to Synthesize Single-Crystalline Zn2SnO4(ZTO) Nanowires and Their Photoluminescence Properties

Effect of Sb-Doped SnO2 Nanostructures on Electrocatalytic Performance of a Pt Catalyst for Methanol Oxidation Reaction