Abstract:Aluminum alloy plates show great potential in energy storage and transportation applications. Nevertheless, the low surface strength of aluminum alloy plates negatively impacts their performance and safety. Aluminum alloys exhibit characteristics such as a low melting point, high reflectivity, and a rapid dilution rate, posing significant challenges for laser cladding coatings. This paper presented the surface modification mechanism of aluminum alloy plates. A stainless steel coating was successfully prepared on the surface of aluminum alloy substrates by using high-speed laser cladding technology. The microstructure, microscopic morphology, and microhardness of the coatings were conducted. The surface and sides of coatings were analyzed by XRD, SEM, EBSD, and microhardness testing, respectively. It is found that larger cellular crystals and carbides predominate at the junction of the substrate and the coating. The middle part of the 0.5-mm coating from the connection and the heat-affected zone are mainly dendritic crystals. The top of the 1-mm coating from the connection is mainly fine crystals. This means that local grain refinement occurs in the stainless steel coating via high-speed laser cladding. There is a transformation of FCC to BCC in the coating. Moreover, the cross-section of the coating exhibits a relatively high microhardness, ranging from 517 to 679 HV. The microhardness at the substrate is measured at 67 HV. The maximum microhardness of the coating is ten times that of the substrate. The bottom of the coating maintains a relatively high microhardness due to the presence of a large amount of carbides. The microhardness of the coating gradually increases from the middle to the surface of the coating. This is primarily attributed to solid solution strengthening and fine grain strengthening mechanisms. Columnar crystals at the metallurgical bond between the substrate and the coating transform into fine grains at the top, leading to a gradual refinement of the microstructure. High-speed laser cladding technology facilitates the enhancement of surface properties and the improvement of surface strength in traditional aluminum alloys.

Progress in strengthening of aluminium alloy surface by laser

A Review of the Laser Cladding of Metal-Based Alloys, Ceramic-Reinforced Composites, Amorphous Alloys, and High-Entropy Alloys on Aluminum Alloys

Laser-based Surface Modifications of Aluminum and its Alloys

The impact of laser surface treatment on the microstructure, wear resistance and hardness of the AlMg5 aluminum alloy

Effect of Laser Strengthening on Electrochemical Corrosion of AA6082 Aluminum Alloy

Microstructure and Application of Surface after Laser Alloying on Surfacing Layer

Superior wear resistance in cast aluminum alloy via femtosecond laser induced periodic surface structures and surface hardening layer

Research and progress of laser cladding on engineering alloys: A review

Uncovering the roles of laser action modes in surface mechanical properties of 2024 aluminum alloy

Tensile Property of 7075 Aluminum Alloy with Strengthening Layer by Laser Remelting-Cladding Treatment

On the laser surface pre-treatment to enhance the surface texture, wettability and adhesion bonding strength of aluminium 7075-T6 laminates

Laser Surface Modification of Aluminium Alloy AlMg9 with B4C Powder

Superior strength-ductility synergy and fatigue resistance of heterogeneous structured AZ41 Mg alloy by laser surface processing

Progress of laser surface treatment on magnesium alloy

Enhancing the corrosion properties and microhardness of titanium alloy by laser surface remelting

Research Progress and Challenges in Laser-Controlled Cleaning of Aluminum Alloy Surfaces

Microstructure and strengthening mechanism of a 316 stainless steel coating prepared by high-speed laser cladding on an aluminum alloy plate

Correlating microstructural features with improved wear and corrosion resistance of laser surface remelted A356 alloy at different scanning speeds

Microstructure and Microhardness of High-Strength Aluminium Alloy Prepared Using High-Speed Laser Fabrication

Influence on the strength and aging resistance of aluminium joints by laser pre-treatment and surface modification

A review of laser additive manufacturing (LAM) aluminum alloys: Methods, microstructures and mechanical properties