Abstract:This paper studies the phenomenon of fiber alignment during the extrusion process. The fiber alignment is largely dependent on shapes of dies and the compression as well as the shear force generated in the extruder. The fiber alignment orientation, of course, would lead to direction dependency of the tensile properties of fiber-reinforced cement (FRC) extrudates. Such a dependency has been investigated in present study. It is found that when fiber volume ratio is small, say 1% of the glass fiber, the majority of the fiber can be aligned in the extrusion direction. As a result, the tensile strength of the thin plate along the extrusion direction is much higher than that along the transverse direction. When the total fiber volume ratio is increased to 2% or 4%, the fiber volume along the transverse direction is largely increased although the percentage of the fiber aligned along the extrusion direction is still higher. Thus, the tensile strength at a transverse direction can be significantly enhanced. In fact, the tensile strength of the samples along the transverse direction is almost the same as that along the extrusion direction when the fiber volume ratio reaches 2%. Furthermore, the strength of the sample at the extrusion direction does not increase proportionally to the fiber volume ratio. For the comparison purpose, plain sheets without any fibers have been prepared by both casting and extrusion. Mechanical properties of the sheets have also been tested and the test results show that extrusion process and fiber addition do have effects on enhancing the tensile properties. Polymer coating on the surface of the samples has also been used to improve the tensile properties of the extrudates with low fiber volume ratio, which shows some promising results.

Extrusion process of lead-clad glass fiber composites

Properties of lead-clad glass fiber composites

Influence of technological parameters on coating speed of Pb-GF composite 'wire

THE PHYSICAL SIMULATION ON EXTRUSION PROCESS OF GLASS FIBER COMPOSITE WIRE COATED BY LEAD

Fiber alignment and property direction dependency of FRC extrudate

Theoretical Derivation and Experimental Verification of Optimal Gap During Extrusion of Composite Wire of Lead Coated on Glass Fiber

Influence of Process Parameters on the Interlaminar Shear Strength of CF/PEEK Composites In-Situ Consolidated by Laser-Assisted Automated Fiber Placement

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Influence of Extrusion Speed on the Microstructure Evolution, Interface Bonding and Mechanical Response of Mg MB26/Al 7075 Composite Rod

Effect of Hot Extrusion on the Microstructure of A Particulate Reinforced Magnesium Matrix Composite

Influences of Extrusion Parameters on Microstructure and Mechanical Properties of Particulate Reinforced Magnesium Matrix Composites

A Study on Hot Stamping Formability of Continuous Glass Fiber Reinforced Thermoplastic Composites

Effect of fabrication parameters on carbon fibre reinforced magnesium matrix composite components

Fiber Breakage and Dispersion during Long Glass Fiber Reinforced Polypropylene Processing

Study on Preparation and Properties of Glass Fiber Reinforced Polylactide

Influence of Extrusion Cycle on the Rheological and Mechanical Properties of Glass Fiber Reinforced PA66 Composites

The effects of processing parameters on the wedge peel strength of CF/PEEK laminates manufactured using a laser tape placement process

Experimental Research of the Influence of Backward Extrusion on the Mechanical Properties of SiCw/6061 Composite

Development and Processing of Continuous Flax and Carbon Fiber-Reinforced Thermoplastic Composites by a Modified Material Extrusion Process

Effect of molding process parameters on the mechanical properties of CGFRPP products