Study on the Influence of Ionic Degree to Gel Breaking and Acid Degradation of P(DMC-AM)
Kui CHEN,Rusheng ZHANG,Jiayuan HE,Jiehua LI,Hong TAN
DOI: https://doi.org/10.19346/j.cnki.1000-4092.2017.02.009
2017-01-01
Abstract:In order to investigate the gel breaking and degradation behavior of cationic polyacrylamide thickener in acid solutions at higher temperature,poly(methacryloyloxyethyl trimethyl ammonium chloride)PDMC,poly(acrylamide)PAM and P(DMC-AM) with ionic degree of 100.0%,0.0%,49.1%,45.9%and 12.7%,respectively,were synthesized under the condition of pH 7.5 and the temperature of 40数60℃with the DMC/AM monomer mass ratio of 12/0,0/12,9/3,6/6,3/9,respectively. The change of solution viscosity of P(DMC-AM)with different cationic degree before and after degradation was explored,and the structural change of P(DMC-AM)before and after degradation were analyzed by IR and 1H-NMR. The results showed that when the five samples were dissolved in acidic liquid(2%or 10%hydrochloric acid)with the mass fraction of 1%,and then was leaved at the temperature of 120℃for 24 h or 48 h,with the increase of ionic degree,the viscosity of P(DMC-AM)solution increased slightly after degradation in general. The steric hindrance effect of cationic side chain could inhibit the degradation,and the higher ionic degree could inhibit gel-breaking. During the degradation process,P(DMC-AM)chiefly occurred backbone scission accompanied by ester bond and amide bond cleavage. Moreover,the degradation of copolymer increased with the increase of the concentration of hydrochloric acid.