Abstract:Tellurite glass has attracted considerable attention and development effort as a host for broad EDFA and EDWA. But the phonon energy of tellurite glass is relatively low as 770 cm~(-1), thus, the~4I_(11/2)→~4I_(13/2) nonradiative decay is too slow to allow pumping at 980 nm. Tungsten-tellurite glass has higher phonon energy of 930 cm~(-1), which makes it possible pumping at 980 nm. The 1.5 μm emission bandwidth of Er~(3+) in tungsten-tellurite glass is also broad. The spectroscopic properties of Yb~(3+)/Er~(3+)-codoped TeO_2-WO_3-ZnO (TWZ) glasses were investigated, too.The Yb~(3+)/Er~(3+)-codoped TWZ glasses were prepared by traditional melting-quenching method. The absorption cross-section was calculated based on measured absorption spectra at room temperature. The emission cross-section was calculated by McCumber theory. The peak values of absorption cross-section and emission cross-section at 1.5 μm are 0.78 pm~2 and 0.90 pm~2, respectively. The 1.5 μm emission spectra, upconversion emission spectra and fluorescence lifetimes of Er~(3+), excited at 970 nm, were also measured. The dependence of Yb~(3+) doping concentration on the 1.5 μm emission and upconversion luminescence of Er~(3+) was studied. The calculated energy transfer efficiency from Yb~(3+) to Er~(3+) in Yb~(3+)/Er~(3+)-codoped TWZ glasses is about 65%. Yb~(3+)-codoping can enhance the 1.5 μm emission intensity effectively. The optimum Yb~(3+) doping concentration is about 7.28×10~(20) ions/cm~3, which is triple of the Er~(3+) doping concentration. The emission bandwidths of Er~(3+) at 1.5 μm in Yb~(3+)/Er~(3+)-codoped TWZ glasses are broad and the obtained full width at half maximum is between 67 nm and 72 nm. Three upconversion emission bands centered at about 533, 547 and 668 nm, were observed. The three emission bands originate from the radiative transitions~2H_(11/2)→~4I_(15/2),~4S_(3/2)→~4I_(15/2) and~4F_(9/2)→~4I_(15/2), respectively. The green and red upconversion emission are both double-photon process. With the increasing of Yb~(3+) doping concentration, the green and red upconversion emission intensity both increase. This can be ascribed to the increased energy transfer rate from Yb~(3+) to Er~(3+).

Spectra Characteristics of Er3+ Doped Nay(Wo4)(2) Crystal

Judd–Ofelt analysis and upconversion emission of Er 3+ –Yb 3+ co-doped oxyfluoride glass ceramics containing LaF 3 nanocrystals

Spectroscopic Properties Of Er3+ Doped Glass Ceramics Containing Sr2gdf7 Nanocrystals

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Spectroscopic properties of Er<sup>3+</sup>and Yb<sup>3+</sup>co-doped glass ceramics containing SrF<sub>2</sub>nanocrystals

Spectroscopic Properties of Er3+–Yb3+ Co-Doped Glass Ceramics Containing BaF2 Nanocrystals

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Energy Transfer and Frequency Upconversion in Er3+-Yb3+ Codoped Oxy-Fluoro-tungstosilicate Glasses

Up-Conversion Luminescence of Nay(Wo4)(2): Yb, Er under 1550 and 980 Nm Excitation

Energy Transfer Upconversion In Er3+ -Doped And Er3+, Ho3+ -Codoped Cs2nagdcl6 Crystals - Art. No. 60280s

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

Spectral Analysis of Er3+-, Er3+/Yb3+- and Er3+/Tm3+/Yb3+-doped TeO2–ZnO–WO3–TiO2–Na2O Glasses

Near ultraviolet to near infrared luminescence spectroscopy of Er 3+ doped K 2 GdF 5 crystal

Optical Transition Probabilities for Er3+ in KY (WO4)2 Crystal

Spectroscopic Properties Of Er3+-Doped Teo2-Wo3-Zno-Znf2 Glasses

Structure, morphology and upconversion luminescence properties of Yb3+/Er3+ Co-doped NaY(WO4)2 phosphors

Energy Transfer Upconversion in Er3+-doped and Er3+, Ho3+-codoped Cs 2 NaGdC1 6 Crystals

Spectroscopic Properties of Yb3 +/er3 + -Codoped TeO2-WO3-ZnO Glasses

Spectral-converting study of Ba((9-3)(m+n)/2)Er(m)Yb(n)Y2Si6O24 (m = 0.005 - 0.2, n = 0 - 0.3) orthosilicate phosphors