As-cast microstructure of 356 aluminum alloy cast by LSC

Jie Dong,Guimin Lu,Qi Feng Ren,Jianzhong Cui

2002-01-01

Abstract:The as-cast microstructure of 356 aluminum alloy cast by liquidus semi-continuous casting (LSC) were studied. When the billet is cast at the normal casting temperature (720°C), the border and center microstructures have coarse dendrites distributed unevenly. When the billet is cast at a temperature (625°C) above the liquidus and the melt alloy is held for 30 min, the border microstructure has small dendrites and the center microstructure has net-spherical grains. When the billet is cast at a temperature (615°C) close to the liquidus and the melt alloy is held for 30 min, the border and center microstructure are the best and there is a little difference between them, but the grains are fine, uniform and globular. The average diameter of the grains are about 25-35 μm and the average circularity is about 1.75-2. The reduction of the primary cooling and casting velocity and the enhancement of the secondary cooling are favorable for the formation of the fine, uniform and globular grains.