Synthesis, Crystal Structure and Reducibility of K2nif4 Type Oxides Sm2-Xsrxcuo4

YH Zhu,H Lou,JG Liu,XJ Liu,FT Ma

DOI: https://doi.org/10.1002/cjoc.20020200410

IF: 5.56

2002-01-01

Chinese Journal of Chemistry

Abstract:K2NiF4 type compounds Sm2-x SrxCuO4 (0 less than or equal to x less than or equal to 1. 2) were prepared. Rietveld refinement of powder diffraction data shows that the crystal system of these compounds belongs to T' type tetragonal structure of space group I4/mmm, and the addition of Sr causes a dramatic shift of the 0(l) ions along the c axis from Sm (Sr) toward Cu while scarcely affecting the Cu-O (11) bond in basal CuO4 plane. From XRD data, it can be seen that when 0.0 less than or equal to x less than or equal to 0.6, Sm2-x Sr-x CuO4 belongs to a single-phase K2NiF4 type structure, while at x greater than or equal to 0.7, both the free SrO phase and the CuO phase exist in these compounds. From the results of XPS and Rietveld refinement, it can be seen that after replacing Sm3+ with Sr2+ of lower valence, the valence of Cu and Sm does not change apparently, and thus some defect must be formed at the oxygen ion positions and/or position A on A(2)BO(4) to keep charge balance and to stabilize the structure.