Abstract:Hierarchical meso-macroporous materials have attracted much attention due to their potential applications in catalysis, sorption, and separation. The incorporation of interconnected macropores in mesoporous materials is very useful because macropores can favor mass transfer and reduce transport limitations. However, it still remains a challenge to fabricate ordered mesoporous channels in the bicontinuous macroporous framework walls. This paper reports a double-templating route based on a sol-gel method to prepare hierarchical meso-macroporous silica monoliths. The obtained material shows a bicontinuous macroporous structure with highly ordered meso-channels distributing inside the macroporous skeleton walls. The bimodal pore structure was formed Under the action of the two templates. The organic polymer was added to induce a phase separation taking place at the sol-gel transition and thus form the bicontinuous macroporous structure. Meanwhile, a nonionic surfactant was introduced to template the formation of ordered mesostructure inside the macroporous skeleton walls. As characterization by scanning electron microscopy, transmittance electron microscopy, N-2,, physisorption, and X-ray diffraction, the resulting silica monolith exhibits Specific Surface area as high as 880 m(2)/g and pore volume as large as 1.2 cm(3)/g. The hexagonally ordered mesopores are highly centered at 5.8 nm. Besides, through optimizing the synthesis procedure, the monolith morphology of the resulting materials can be perfectly preserved during the wet gel drying process, and thus a crack-free hierarchical silica monolith with centimeter scale can be obtained.

Synthesis of ordered mesoporous carbon monoliths with bicontinuous cubic pore structure of Ia3d symmetry.

Synthesis of ordered mesoporous carbon monoliths with bicontinuous cubic pore structure of Ia3d symmetryElectronic supplementary information (ESI) available: experimental section and further characterisation data (Fig. S1???4). See http://www.rsc.org/suppdata/cc/b2/b209233f/

The Unusual Electrochemical Characteristics of A Novel Three-Dimensional Ordered Bicontinuous Mesoporous Carbon

Electrochemical properties of an ordered mesoporous carbon prepared by direct tri-constituent co-assembly

Mesoporous Carbon Materials: Synthesis and Modification.

Facile Synthesis of Transparent Mesostructured Composites and Corresponding Crack-Free Mesoporous Carbon/Silica Monoliths

Synthesis, Characterization and Application of Novel Bicontinuous Mesoporous Silica with Hierarchical Pore Structure

Synthesis of Ordered Three-Dimensional Large-pore Mesoporous Silica and Its Replication to Ordered Nanoporous Carbon

Synthesis of Large-Pore Periodic Mesoporous Organosilica (PMO) with Bicontinuous Cubic Structure of Ia–3d Symmetry

A Facile Synthesis of Highly Ordered Mesoporous Carbon Monolith with Mechanically Stable Mesostructure and Superior Conductivity from SBA-15 Powder

Controlled Synthesis of the Tricontinuous Mesoporous Material Ibn-9 and Its Carbon and Platinum Derivatives

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Synthesis and Electrochemical Properties of Semicrystalline Gyroidal Mesoporous Mno2

A Facile Aqueous Route To Synthesize Highly Ordered Mesoporous Polymers And Carbon Frameworks With Ia(3)Over-Bard Bicontinuous Cubic Structure

Synthesis of Carbon Replicas of Sba-1 and Sba-7 Mesoporous Silicas

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Constructing Unique Mesoporous Carbon Superstructures via Monomicelle Interface Confined Assembly

Controlled Synthesis of Porous Carbon Nanostructures with Tunable Closed Mesopores via a Silica-Assisted Coassembly Strategy

A Novel Mesoporous Carbon@silicon-Silica Nanostructure for High-Performance Li-ion Battery Anodes.

Synthesis and Phase Behaviors of Bicontinuous Cubic Mesoporous Silica from Triblock Copolymer Mixed Anionic Surfactant