Synthesis And Dielectric Properties Of A New Niobate Sr5ndti3nb7o30

H Zhang,Xk Hong,L Fang,Fc Meng,Hx Liu

DOI: https://doi.org/10.3321/j.issn:1001-4861.2002.11.012

2003-01-01

Chinese journal of inorganic chemistry

Abstract:A new niobate Sr5NdTi3Nb7O30 was synthesized in the SrO-Nd2O3-TiO2-Nb2O5 system by solid state reaction at 1350degreesC for 48h. The structure and dielectric properties of Sr5NdTi3Nb7O30 were determined by X-ray powder diffraction, scanning electron microscope and dielectric measurements. The results show that Sr5NdTi3Nb7O30 belongs to ferroelectric, phase of filled tetragonal tungsten bronze structure at room temperature with unit cell parameters: a = 1.23084(4) nm, c = 0.38794(2) nm, space group P4 bm, calculated density 5.245g (.) cm(-3). Sr5NdTi3Nb7O30 belongs to relaxor ferroelectrics. The phase transition temperature (T-c) of Sr5NdTi3Nb7O30 from ferroelectric to paraelectric is found to shift toward higher temperature side at higher frequency, and T-c is 180degreesC at 1 kHz. At room temperature, the dielectric constant (epsilon(r)) Sr5NdTi3Nb7O30 is nearly independent of frequency, and Sr5NdTi3Nb7O30 ceramic has high dielectric constant 288 at 1 MHz and low dielectric loss of 0.0022.