Abstract:Magnesium hydride (MgH2) offers large capacity for hydrogen storage, but poor thermodynamics and kinetics for releasing hydrogen. In this work, the novel 1D bamboo-shaped carbon nanotubes (BCNTs) are firstly used as carriers for the self-assembly of MgH2 (denoted as MgH2@BCNTs). The high specific surface area (262.3 m(2)g(-1)) and large diameter (over 80 nm) of BCNTs contribute to extremely high loading capacity (76.8 mass fraction), small particle size (15-20 nm) and uniform distribution of MgH2 nanoparticles (NPs). The well-defined MgH2@BCNTs shows remarkably improved thermodynamics and kinetics for H-2 adsorption and desorption. In particular, it starts to release hydrogen at about 220 degrees C, near 170 degrees C lower than that of the commercial MgH2, as well it tends to be hydrogenated even at a relatively low temperature of 100 degrees C by absorbing 3.56 wt% H-2. Moreover, a reversible capacity up to 5.79 wt%, including the "dead weight" of BCNTs, and is well maintained after 10 cycles. The dehydrogenation E-a and Delta H of MgH2@BCNTs can be reduced to 97.97 kJ/mol and 68.92 kJ/mol, which are 111.24 kJ/mol and 6.07 kJ/mol lower than those of the commercial MgH2, respectively. By high pressure densification treatment, the MgH2@BCNTs system achieves an exceptional volumetric capacity up to 65.90 g/L without obvious performance degeneration, resulting from the special structure of BCNTs with inner intervals which works as supports under ultra-high pressure of 750 MPa. Our innovative design of 1D BCNTs supporting MgH2 NPs with high loading weight offers new strategy to synchronously improve the gravimetric and volumetric capacity, as well as the hydrogen storage kinetics and thermodynamics of the nanoconfinement system in the future.

Hydrogen Storage in Carbon Nitride Nanobells

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

Hydrogen Adsorption in Bundles of Well-Aligned Carbon Nano Tubes at Room Temperature

Hydrogen Storage in Carbon Nanotubes Through the Formation of Stable C-H Bonds.

Pore Structure And Hydrogen Storage Of Carbon Nanotubes

Hydrogen storage of dense-aligned carbon nanotubes

Interaction of Hydrogen with Metal Nitrides and Imides

Hydrogen Storage in Multi-Wall Carbon Nanotubes Using Samples Up to 85 G

Nanoporous adsorbents for hydrogen storage

Acid-assisted synthesis of nitrogen-deficient mesoporous graphitic carbon nitride for hydrogen storage

Synergetic Action of 0D/2D/3D N-doped Carbon Nanocages and NbB2 Nanocatalyst on Reversible Hydrogen Storage Performance of Lithium Borohydride

Carbon and Boron Nitride nanostructures for Hydrogen storage applications through a theoretical perspective

Carbon composite support improving catalytic effect of NbC nanoparticles on the low-temperature hydrogen storage performance of MgH2

Computational Evaluation of Li-doped g-C2N Monolayer as Advanced Hydrogen Storage Media

Geometry, Electronic Properties, and Hydrogen Adsorption Properties of Li3n-Based Nanostructures

Potential of AlN Nanostructures As Hydrogen Storage Materials

Hydrogen Adsorption of Open-Tipped Insufficiently Graphitized Multiwalled Carbon Nanotubes

Polymerized Carbon Nitride Nanobells

Hydrogen Storage in Heat-Treated Carbon Nanofibers Prepared by the Vertical Floating Catalyst Method

Computational exploration of magnesium-decorated carbon nitride (g-C3N4) monolayer as advanced energy storage materials

In Situ Ni-Doped Hierarchically Porous Carbon Nanofibers Derived from Polyacrylonitrile/Pitch for Hydrogen Storage at Ambient Temperature