Microstructure and strength of laser welds of sub-micron particulate-reinforced aluminum matrix composite Al2O3p/6061A1

Liming Liu,Jitai Niu

IF: 6.318

2001-01-01

Rare Metals

Abstract:The microstructure of laser welds of sub-micron particulate-reinforced aluminum matrix composite Al2O3p/6061Al and the weldability of the material were studied. Experimental results indicated that because of the huge specific surface area of the reinforcement, the interfacial reaction between the matrix and the reinforcement was restrained intensively at elevated temperature and pulsed laser beam. The main factor affecting the weldability of the composite was the reinforcement segregation in the weld resulting from the push of the liquid/solid interface during the solidification of the molten pool. The laser pulse frequency directly affected the reinforcement segregation and the reinforcement distribution in the weld, so that the weldability of the composite could be improved by increasing the laser pulse frequency. On the basis of this, a satisfactory welded joint of sub-micron particulate-reinforced aluminum matrix composite Al2O3p/6061Al was obtained by using appropriate welding parameters.