Influence of Cu content on interfacial structure and mechanical properties of 3Al2O32SiO2 fiber reinforced Al matrix composites
Lin Geng,Hong Yu Xu,Jun Xiang Wang,Zhen Zhu Zheng,Ku Ai Yu
DOI: https://doi.org/10.4028/www.scientific.net/KEM.313.165
2006-01-01
Key Engineering Materials
Abstract:In this paper, pure aluminium and Al-Cu (1%, 3% and 5% in mass fraction) alloy matrix composites reinforced with 35vol% 3Al(2)O(3)2SiO(2) short fibers were fabricated by a squeeze-casting technique. Interfacial structure and distribution of element of the composites were investigated by means of SEM, EPMA and TEM. The experimental results indicated that when pure aluminium was used as matrix, the interface was slick and chemical reaction occurred at the interface between amorphous SiO2 and matrix Al. When Cu element was added into the Al matrix alloy, the amorphous SiO2 on the fiber surface remained. Further more, with the increase of Cu element, the amount of the retained amorphous SiO2 increased. The interfacial reaction was inhibited due to the Cu element diffusion and enrichment towards the short fiber surface. SEM observation showed that large amount of fiber was drawn out from the matrix and some of them have been ruptured. Tensile test showed that the tensile strength of the 35vol% 3Al(2)O(3)2SiO(2sf)/Al-Cu composite increased with the increasing of Cu content as compared with the Al2O3f/pure Al composite, the increment of the fracture strength of 3Al(2)O(3)2SiO(2sf)/Al-Cu composite were 102%, 146% and 171%, respectively.