Synthesis and Characterization of Epoxy Resin Modified with Nano-Sio2 and Γ -Glycidoxypropyltrimethoxy Silane
Haiyan Li,Zhisheng Zhang,Xiaofei Ma,Ming Hu,Xiuyu Wang,Panfeng Fan
DOI: https://doi.org/10.1016/j.surfcoat.2006.07.143
IF: 4.865
2007-01-01
Surface and Coatings Technology
Abstract:Epoxy resin has been modified with nano-SiO2, standard SiO2, particles with diameter 30-40 nm and 3 gm, respectively, and gamma-glycidoxypropyltrimethoxy silane. IR spectra indicated bonded stationary phase was formed with gamma-glycidoxypropyltrimethoxy silane between nano-SiO2, and epoxy resin. Thermogravimetric analysis, impact strength and bulk resistivity tests showed that initial decomposition temperature T-d, impact strength and bulk resistivity of epoxy resin-based composite increased and then decreased after nano-SiO2 content reached 4 wt.%, optimal values were 323 degrees C, 89.2 kJ m(-2) and 3.56 x 10(14) Omega cm, respectively. Similar behavior had been also observed on standard SiO2,/epoxy resin-based composites, optimal values were 308 degrees C, 17.13 kJ m(-2) and 2.80 x 10(14) Omega cm, respectively. SEM analysis showed that toughness of nano-SiO2,/epoxy resin-based composite and standard SiO2,/epoxy resin-based composite also increased and then decreased after nano-SiO2 and standard SiO2, content reached 4 wt.%. (C) 2006 Elsevier B.V. All rights reserved.