Abstract:The PLA-g-(GMA-co-St) graft copolymer (PGS) was prepared using melt-free radical grafting technology, PGS and ESO were simultaneously employed as compatibilizers for the poly (lactic acid)/poly (butylene adipate- co -terephthalate) (PLA/PBAT) blends. The effects of the type and amount of compatibilizers on the properties of the blends were studied. The results reveal that the epoxy groups in PGS and ESO can interact with the terminal groups of PLA and PBAT. The incorporation of either PGS or ESO separately can improve the compatibility between PLA and PBAT to a considerable degree. However, the introduction of both compatibilizers into the PLA/PBAT blends results in a notable shift of the T g of the two phases, reduces the size of PBAT particles, and makes their dispersion more uniform. This reveals that the dual reactive compatibilizers can achieve a synergistic effect, significantly reduced the interfacial tension between the two phases and facilitated inter-phase dispersion, ultimately forming a more uniform microstructure. Simultaneously, as the amount of ESO added to the blends gradually increase, the vicat softening temperature and complete decomposition temperature of the blends continue to increase, the notched impact strength and elongation at the break of the blends gradually increase and then decrease. When the ESO amount reaches 4 wt%, the performance of each property increases to 88.9 °C, 447.66 °C, 335.16 %, and 23,359.30 J/m 2 , respectively. At this point, the fracture surface of the blend samples is accompanied by a large-scale plastic deformation. In conclusion, this work represents the first attempt to accomplish synergistic effects via dual reactive compatibilizers. Under the best formulation and processing circumstances, the PLA/PBAT blends greatly increase their overall performance while maintaining biodegradability, hence broadening their application prospects in packaging, agriculture, and disposable tableware.

Novel Blends of Poly[Bis(Glycine Ethyl Ester) Phosphazene] and Polyesters or Polyanhydrides: Compatibility and Degradation Characteristics in Vitro

In Vitro and in Vivo Degradation Study on Novel Blends Composed of Polyphosphazene and Polyester or Polyanhydride

Compatibility and degradation of novel polyphosphazene/polyanhydride blends

Poly(glycolic Acid) Materials with Melt Reaction/processing Temperature Window and Superior Performance Synthesized Via Melt Polycondensation

[In Vivo Degradation and Tissue Compatibility of Polyphosphazene Blend Films].

Preparation, Characterization and Degradation Characteristics of Polyanhydrides Containing Poly(Ethylene Glycol)

Novel Biodegradable Polyphosphazenes Containing Glycine Ethyl Ester And Benzyl Ester Of Amino Acethydroxamic Acid As Cosubstituents: Syntheses, Characterization, And Degradation Properties

Studies on the Miscibility of Poly[bis(glycine ethyl ester)phosphazene]/Polyesters Blends

Novel biodegradable polyphosphazenes containing glycine ethyl ester and benzyl ester of amino acethydroxamic acid as cosubstituents

Effect of poly(lactic-co-glycolic acid) blend ratios on the hydrolytic degradation of poly(para-dioxanone)

Regulation of Biodegradability and Drug Release Behavior of Aliphatic Polyesters by Blending

Modulating Drug Release from Short Poly(ethylene Glycol) Block Initiated Poly(L-lactide) Di-block Copolymers

[Preparation, Characterization and Drug Release Characteristics of Poly(lactide)(pl)/poly(lactide-Co-polyethylene Glycol)(pleg) Blend Microspheres].

Physical and degradation properties of binary or ternary blends composed of poly (lactic acid), thermoplastic starch and GMA grafted POE

Short Poly(ethylene Glycol) Block Initiation of Poly(l‐lactide) Di‐block Copolymers: a Strategy for Tuning the Degradation of Resorbable Devices

Effect of glycidyl methacrylate-grafted poly(ethylene octene) on the compatibility in PLA/PBAT blends and films

Accelerated hydrolytic degradation of poly(l-lactide) by blending with poly(ether-block-amide)

Highly toughened poly (lactic acid)/poly (butylene adipate-terephthalate) blends in-situ compatibilized by MMA-co-GMA copolymers with different epoxy group content

Cellular Compatibility of Blends Consisting of Poly (3-Hydroxybutyrate-co-3-hydroxyhexanoate) and Polyethylene Glycol

Synthesis, physical properties and biocompatibility of poly[di(ethyl glycinato) phosphazene]

Synergistic effects of dual reactive compatibilizers for high-performance fully biodegradable polylactic acid/poly (butyleneadipate-co-terephthalate) composites