Abstract:The crystal structure and its relationship with the high piezoelectric performance of PbZr1-xTixO3 (PZT) have been studied for years, especially near the morphotropic phase boundary (MPB). Now the bridging monoclinic Cm phase in the MPB separating the not-group-subgroup-related R3c and P4mm has been widely accepted. However, in recent high-resolution powder diffraction experiments and Rietveld refinement analyses, the presence of the monoclinic Cm phase was found across the whole composition from the MPB to the rhombohedral region. Around the MPB, the structure seems to become more complicated, with a mixture of three phases[1]. It was also found that the local structure of PZT can be different from its average structure by examining the anisotropic displacement ellipsoids of both Pb and O: 1) the Pb atoms in the rhombohedral phase are displaced away from the threefold symmetry axes to create locally monoclinic symmetry that averages out to form an overall rhombohedral symmetry[2]; 2) at high temperature, the local effect of the low-temperature oxygen octahedra tilts remained even in the cubic phase[3]. In order to better study the local structures of PZT, we have carried out a series of high-resolution neutron diffraction experiments on both powder samples using Pair Distribution Function (PDF) analysis and single crystal samples using Diffuse Scattering (DS) analysis. The difference between the average and local structures is confirmed. The local distribution of the Pb displacements directions are plotted out for different compositions in PZT (x = 0.20, 0.30 and 0.40), which reveals on approaching MPB, the Pb atoms are tend to displace on one monoclinic mirror plane forming a macroscopic monoclinic phase. This is the first time that the local monoclinic short range order in Zr-rich PZT has been observed.

Influence of PbZrO3 on the diffuse phase transition of PZN-PZ-PT solid solution

The Influence of PbZro3/PbTio3 Ratio on Diffuse Phase Transition of Pb(Zn1/3Nb2/3)O3–PbZro3–PbTio3 System Near the Morphotropic Phase Boundary

Synthesis, Structure, and Properties of the PbZrO3-PbTiO3-Bi(Zn2/3Nb1/3)O-3 Ternary Solid Solution System Around the Morphotropic Phase Boundary

Synthesis, Structure and Electric Properties of a Novel Solid Solution System: (1-X)pb(zr0.52ti0.48)o-3-xbi(zn2/3nb1/3)o-3

Diffusion in Multi-Compositional Pz-Pt-Pzn Ceramics Prepared by Spark Plasma Sintering

Local Study on the Composition and Temperature Induced Structural Change of Pzt

Phase Transformation Behavior and Electrical Properties of Pb(Zr0.56Ti0.44)O3–Bi(Zn0.5Ti0.5)O3 Solid Solution Ceramics

A new Pb(Lu1/2Nb1/2)O3-PbZrO 3-PbTiO3 ternary solid solution with morphotropic region and high Curie temperature

A Neutron Diffuse Scattering Study of Pbzro3 and Zr-Rich Pbzr1-Xtixo3

Morphotropic Phase Boundary in Pb(Ni1/3Nb2/3)O3–PbTiO3 Solid Solution System

REACTION MECHANISM IN PHASE FORMATION OF PbZrxTi1-xO3 PREPARED BY A TWO-STAGE PRECIPITATION ROUTE

The Influence of the Morphotropic Phase Boundary on the Dielectric and Piezoelectric Properties of the Pnn-Pz-Pt Ternary System

Phase structure and electrical properties of x PZN–(1− x )PZT piezoceramics near the tetragonal/rhombohedral phase boundary

Study of Phase Transition and Domain Evolution Behavior in Pzn-Pt Single Crystal

Retailoring the morphotropic phase boundary to enhance the electric performance by adjusting Zr/Ti ratio in Pr-doping PZT system

Phase Transition Hysteresis at the Antiferroelectric-Ferroelectric Boundary in PbZr1−xTixO3

Local-scale structures across the morphotropic phase boundary in PbZr1- x Ti x O3

Composition-driven structural phase transition in ferroelectric PbZrxTi1-xO3 across the morphotropic phase boundary

Higher wavenumber shift of Pb (Al1/2Nb1/2)O3 substitution in relaxor ferroelectric Pb(Zr0.52Ti0.48)O3-Pb(Zn1/3Nb2/3)O3 ceramics

Study of A New Antiferro-/Ferro-electric Solid Solution: PbZrO3-Pb(Zn½W½)O3

Review of the recent x-ray and neutron powder diffraction studies on lead zirconate titanate