Transient Relaxation of Optical Transmissivity of Composite Thin Films with Different Nano-Scale Ag Particles

JL Wu,CM Wang,QF Zhang,BX Xu,YH Zou

DOI: https://doi.org/10.1117/12.405297

2000-01-01

Abstract:The development of photon devices requires the materials with high optical response speed. A type of composite thin films composed of nano-scale Ag particles and barium oxide medium was fabricated. There were two methods in the formation of the thin films: single metallic layer method and triple metallic layer method. The thickness of the thin films in different formation methods was approximately 150 nm or 300 nm, while, Ag particles had an average diameter of 20 nn or 15 nm. A pump-probe method was used for measuring the transient change of optical transmissivity of thin films which were stimulated by ultrashort laser pulses of duration 150 fs and wavelength 647 nm. The Ag-BaO thin films presented that the transmissivity increased rapidly. The thin films containing smaller metallic Ag particles with average diameter of 15 nm exhibited shorter relaxation time of the optical transmissivity with 1.6 ps, but the thin films containing particle diameter of 20 nm resulted in an optical relaxation time of 2.0 ps. Optical relaxation is a process in which nonequilibrium electrons, excited by laser pulses and originating from nano-scale metallic particles, return to the equilibrium state. The Ag-BaO thin films, with extremely fast optical response time, are promising materials for high speed optical devices.