Photoconductivity and structural characterization of fullerenated PVKBr polymer
Zu-En Huang,Yu Chen,Rui-Fang Cai,Wei-Wen Ma,Xiu-Feng Hou,Qianfen Shao,Feiling Zhao,Dezheng Fu,Guosun Shi,Xiaoliang Sheng,Wei Jin,Shou-Tai Wang,Dao-Cheng Pan
DOI: https://doi.org/10.1016/S0022-3697(96)00091-1
IF: 4.383
1997-01-01
Journal of Physics and Chemistry of Solids
Abstract:The influence of chemical modification (fullerenation) on structure and photoconductivity in brominated poly(N-vinylcarbazole)(PVKBr) has been described. The characterization techniques employed are UV-Visible, FT-IR, TGA, DTG, 13C CP/MAS NMR, XRD and SEM. The fullerenated PVKBr has a visibly deep-brownish yellow cast when compared with the unreacted polymer PVKBr. Its UV-Visible absorption spectrum, in which the main bands center at 191, 195, 215, 229, 240, 250, 265, 297, 331 and 345 nm, tends to move to the longer wavelength in compared that of the PVKBr and the peak range also extended from about 300 to 860 nm. The X-ray diffraction evidence indicated that X-ray diffraction structure of fullerenated PVKBr differs greatly from that of PVKBr arising from the covalent attachment of C60 to the brominated PVK backbone. The decreased photogeneration efficiency of fullerenated PVKBr might be thus linked to this conformational complication. The photo-induced discharge rates of pure PVK, PVKBr, C60-PVK, and C60-PVKBr are found qualitatively in the following order: 3.85% C60-PVK ⪢ PVKBr > 3.85%C60-PVKBr > pure PVK under the same experimental conditions.