A New Generation of Poly(lactide/ε-Caprolactone) Polymeric Biomaterials for Application in the Medical Field.
J. Fernandez,A. Larranaga,A. Etxeberria,W. Wang,J. R. Sarasua
DOI: https://doi.org/10.1002/jbm.a.35036
2013-01-01
Journal of Biomedical Materials Research Part A
Abstract:Thermoplastic biodegradable polymers displaying an elastomeric behavior are greatly valued for the regeneration of soft tissues and for various medical devices. In this work, terpolymers composed of ε-caprolactone (CL), D-lactide (D-LA), and L-lactide (L-LA) were synthesized. These poly(lactide-ε-caprolactone) (PLCLs) presented an elevated randomness character (R∼1), glass transition temperatures (Tg ) higher than 20°C and adjusted L-LA content. In this way, the L-LA average sequence length (/L-LA ) was reduced to below 3.62 and showed little or no crystallization capability during in vitro degradation. As a result, the obtained materials underwent homogenous degradation exhibiting KMw ranging from 0.030 to 0.066 d(-1) and without generation of crystalline remnants in advanced stages of degradation. Mechanical performance was maintained over a period of 21 days for a rac-lactide-ε-caprolactone copolymer composed of ∼85% D,L-LA and ∼15% CL and also for a terpolymer composed of ∼72% L-LA, ∼12% D-LA and ∼16% CL. Terpolymers having L-LA content from ∼60 to 70% and CL content from ∼10 to 27% were also studied. In view of the results, those materials having CL and D-LA units disrupting the microstructural arrangement of the L-LA crystallizable chains, an L-LA content <72% and a random distribution of sequences, may display proper and tunable mechanical behavior and degradation performance for a large number of medical applications. Those with a CL content from 15 to 30% will fulfill the demand of elastomeric materials of Tg higher than 20°C whereas those with a CL content from 5 to 15% might be applied as ductile stiff materials.