The Effects of Structure of <i>N</i>-heterocyclic Monomers on the Performance of Copoly(aryl ether ketone ketone)s
Qian Liu,Zhao-qi Wang,Xiao-qing Yang,Kai-wen Wu,Shao-kui Fu,Xu Wang,Shou-hai Zhang,Xi-gao Jian
DOI: https://doi.org/10.11777/j.issn1000-3304.2021.21032
2021-01-01
Acta Polymerica Sinica
Abstract:4,4'-Diphenyl-6,7'-biphthalazin-1,1'(2H, 2'H)-dione (6,7-DBD) and 4,4'-diphenyl-7,7'-biphthalazin 1,1' (2H,2'H)-dione (7,7-DBD) were synthesized. The copolymerization behaviors of two DBDs and 4-(4-hydroxyphenyl)2,3-phthalazin-1-one with 1,4-bis(4-fluorobenzoyl)benzene were investigated, separately. N-heterocyclic copoly (aryl ether ketone ketone)s with different locations of side-phenyl groups (P-CDs and P-TDs) were obtained. The intrinsic viscosities (eta(int)) of the copolymers are in the range of 0.5-1.1 dL/g. P-CDs perform the easier preparation process and higher eta(int) than P-TDs. The glass transition temperature of P-CDs ranges from 254 degrees C to 296 degrees C, and the retention rate of storage modulus is up to 67% at 250., which is higher than that of P-TDs with the similar polymerization composition. Both copolymers are soluble in commom solvent, such as N-methylpyrrolidone and 1,1,2,2-tetrachloroethane. The tensile modulus is in the range of 1.56-1.78 GPa, the tensile strength is in the range of 50.1-102.9 MPa, the elongation at break is in the range of 11.0%-18.1%, and the insulation properties are little short of the same. In summary, P-CDs exhibit better heat resistance, solubility, and mechanical proteties than P-TDs. It can be found that adjusting the distribution of side phenyl in main chains can significantly affect the thermal stability, mechanical property, solubility, and preparability of the polymer, which provides an attempt direction for the preparation of high-performance polymers with high heat resistance and solubility.