A one-step process to produce high-crystallinity cellulose microfibrils from microwave irradiation of natural fiber waste
G. Y. Romero-Zúñiga,S. Sánchez-Valdés,M. A. Ceniceros-Reyes,I. Sifuentes-Nieves,C. A. Gallardo-Vega,S. G. Solís-Rosales,P. González-Morones,E. Hernández-Hernández
DOI: https://doi.org/10.1007/s10570-023-05493-1
IF: 6.123
2023-09-17
Cellulose
Abstract:The present investigation demonstrated that through microwave treatment of natural fiber wastes, cellulose microfibrils with a purity of 86.82% by weight, a crystallinity percentage of 92.5%, lengths from 1 to 15 mm, and diameters between 7 and 12 μm are obtained. These results were obtained with a one-step methodology, where Agave fibers were suspended in ethylene glycol and irradiated for 5 min with a constant power of 200 W and temperature of 250 °C. In-situ analyses (heating rate, pressure, and aspect ratio of the reaction vial) performed during microwave irradiation, as well as the characterization (thermal, chemical, and morphological) of the treated agave fibers, indicated that dielectric heating of the components of the agave fibers (waxes, pectin, hemicellulose, lignin) produces their depolymerization and leaching towards the reaction medium (ethylene glycol) until their defibration is achieved. The reaction kinetics at different temperatures and times showed that the purification of the fibers starts at 12,000 W. However, to finally obtain the microfibrils, it is necessary to apply 69,812 W. This process has the advantage that the fiber does not have to be treated with chemical substances or mechanical processes before the microwave treatment. Moreover, no additives, reducers, or catalysts are used during or after the treatment, which makes it a novel and optimal process to produce highly pure and crystalline cellulose microfibrils for high-value-added applications.
materials science, textiles,polymer science, paper & wood