Abstract:PrBa2Cu3O7-y (PrBCO) is unique in the RBa2Cu3O7-y (R = rare earth) series because it is not superconducting. In fact, for Y1-xPrxBa2Cu3O7-y, T-c drops monotonically with Pr concentration, with T-c going to zero at 55% Pr. There have been many studies of this material with the hope that an explanation for the lack of superconductivity in PrBCO might help explain why YBa2Cu3O7-y is superconducting. Unfortunately, to date, none of the proposed explanations has been totally satisfactory and without objection due to the considerable controversy of the results obtained by different experiments. In this paper, a series of samples of Y1-xPrxBa2Cu3O7-y (YPrBCO) (0 less than or equal to x less than or equal to 0.55) have been studied by x-ray diffraction, Raman spectroscopy and XPS. The results reveal that the Pr dopant does not change the orthorhombic symmetry of the samples. The peak positions at 502 and 334 cm(-1) of the Raman spectra become shifted for different Pr concentration, which suggests a change in oxygen content upon substitution of Pr ion for Y ion. There are two valences of Pr ions in YPrBCO. The valence of Pr is changed with change in Pr content x. The relative content of Pr3+ and Pr4+ is closely related to the total Pr content x. The valence of Pr is close to 3+ for small x, and is increased as x increases. The valence change of the Pr ion would directly result in the increase of oxygen content. A ligand hole localized on the Pr-O(2)/O(3) band would remove a hole from the conduction band and yield a formal Pr4+ site. The strong hybridization between Pr 4f electrons and conduction holes in the CuO2 planes induces a localization of mobile holes causing the suppression of superconductivity in the YPrBCO system. In addition, the existence of some extra oxygen atoms around Pr wilt also affect the distortion of the CuO2 planes and possibly assist in the suppression of the superconductivity.

A quantitative understanding for the Tc suppression in Y1−xPrxBa2Cu3O7

Hole Distribution Andtcsuppression Iny1−x

Site-specific Electronic Structure of Pr Inpr1+xba2−x

Origin of the ionic size effect on Pr-induced Tc suppression in R1−xPrxBa2−ySryCu3O7-δ

BOND VALENCE CHARACTER AND SUPERCONDUCTIVITY IN Y1-xPrxBa2Cu3O7-δ SYSTEM

Suppression of Superconductivity in the Y1−xPrxBa2Cu2.95Li0.05O7-δ System

Planar 17O NMR study of Pr_yY_{1-y}Ba_2Cu_3O_{6+x}

Origin of the ionic size effect on Pr-induced T-c suppression in R1-xPrxBa2-ySryCu3O7-delta

Rare-earth Ionic Size Effects on Tc in the Series RBa2Cu3O7-σ

Positron Annihilation Study of Y1−xPrxBa2Cu3O7

Mechanisms Of Substitution Effects On Different Lattice Sites In Yba2cu3o7-Y

Electronic Property and Structure of Double-Doping Y1−2xPrxCaxBa2Cu3O7−δ with 0⩽X⩽0.14

Rare-earth ionic size effects on T-c in the series RBa2Cu3O7-delta

Investigation of Hole Distribution in Y 1-X Pr X Ba 2 Cu 3 O 7

Different effects of Zn and Pr doping on YBa2Cu3O7−y

Nernst Effect in Oxygen-Depleted SmBa2Cu3O6+x Single Crystals

Magnetic Properties of a High T C Superconductivity Related System Y1−xPrxBa2Fe3O8

Hole Filling And Interlayer Coupling In Bi2sr2ca1-Xprxcu2oy Single Crystals

SUBSTITUTION EFFECT IN <font>Pr</font>-DOPED YBCO

Study on the crystal and electronic structure of Y1-xPrxBa2Cu3O7-y ceramics

SUBSTITUTION EFFECT IN Pr-DOPED YBCO