Abstract:Eu-doped nanocrystalline Lu2O3 with different particle sizes was prepared by combustion synthesis. The local structures around the rare-earth Lu and Eu ions were studied by using both Lu and Eu L-3 edge X-ray absorption spectroscopy. According to the extended X-ray absorption fine structure (EXAFS) analysis, detailed local structure information such as coordination numbers, bonding length, and disorder has been obtained. The results showed that the samples with a particle size larger than 5 nm keep the cubic structure and the disorder increases with decreasing size. However, when the particle size is smaller than 5 nm, the existence of considerable amorphous components accounts for the rough interface and the obvious change of the local structure around the rare-earth ions. A new type of coordination environment around Eu was formed, and the most probable symmetry of the Eu3+ site was determined by combining the real-space self-consistent field full multiple scattering X-ray absorption near edge structure (XANES) calculation and the EXAFS result. The local structure information obtained from EXAFS and XANES was used to explain the size-dependent luminescent properties of the nanocrystalline Lu2O3:Eu. The decreasing intensity ratio between the host absorption band and the Eu3+-O2- charge-transfer state (CTS) band with decreasing particle size can be attributed to a larger disorder and more defects in the small sized samples, while the red shift of the CTS band in the smaller size particles can be ascribed to the longer Eu-O bond length and the higher coordination number.

Extended X-Ray Absorption Fine Structure Study of Eu-Doped Bapbo3

Formation of BaPbO3 and its EXAFS study

Comparative investigations of the crystal structure and photoluminescence property of eulytite-type Ba3Eu(PO4)3 and Sr3Eu(PO4)3.

Crystal Structure and Eu3+/Tb3+ Doped Luminescent Properties of a New Borate Ba3BiB9O18

Nanocrystalline Eu-doped PrB6 Hexaborides with Tunable Optical Absorption: A Combined Experimental and Density Functional Theory Study

XAFS at Eu–L3 edge and UV–VUV excited luminescence of europium doped strontium borophosphate prepared in air

Studies on the electronic structure and bonding of EuB6 and calculation of its optical constants

EXAFS Study on the Lanthanum Ion Doped PbWO4 Crystal

Local Structure Around Reduced Rare Earth Ions Doped in Borate Glasses by XAFS

[Effect of Eu(Pr) Substitution at Ba Sites on Microstructure and Superconductivity in EuBa2Cu3O7-delta Ceramics].

Structures and Optical Properties of Eu^3＋ Ion Doped Zinc-alumino-silicate Glass-ceramics

Structure and luminescent properties of electrodeposited Eu 3 + -doped CaF 2 thin films

Site Occupancies, VUV-UV-vis Photoluminescence, and X-ray Radioluminescence of Eu2+-Doped RbBaPO4

Structure and Transport Properties in YBa2−xEuxCu3O7−δ Superconductors

Exafs Study the Local Structure of Nanocrystalline Lu2o3 : Eu

Structural and luminescent properties of Eu3+ doped Gd17.33(BO3)4(B2O5)2O16

Local Structure of Nanocrystalline Lu2O3:Eu Studied by X-ray Absorption Spectroscopy

VUV Excited Luminescence of Europium Activated Calcium Borophosphate Prepared in Air

Vuv And Eu-L-3 Edge Xanes Spectra Of Europium-Doped Strontium Tetraborate Prepared In Air

Mixed occupation, double valence and tunable emission of Eu in BaIn2(P2O7)2

Structural and luminescent properties of LnBaB9O16:Eu3+